Preparation of novel marine antifouling polyurethane coating materials

Chen, Meilong, Kang, Yonghai, Guo, Yuanjun, Guo, Yan, Yan, Jianhui, Li, Duxin, Liu, Qingquan, Ou, Baoli, Zhang, Shanggao

2018

نظرة عامة

Polyurethane coating materials with different compositions of low surface energy polydimethylsiloxane and degradable poly( l -lactic acid) were synthesized by three major steps. Initially, the hydroxylation-terminated poly( l -lactide)-functionalized graphene (G- g -PLLA) was prepared by ring-opening polymerization of l -lactic acid using the phenol-functionalized graphene (G-f-OH), which was prepared by 1,3-dipolar cycloaddition reaction of graphene and 3,4-dihydroxybenzaldehyde when N -methylglycine and tin octoate were used as initiator and catalyst, respectively. Subsequently, isocyanate-terminated polyurethane prepolymer with polydimethylsiloxane was obtained by condensation polymerization of polydimethylsiloxane and isocyanate-terminated polyurethane prepolymer that was obtained by the condensation polymerization of 4,4′-diphenylmethane diisocyanate and 1,4-butane diol. Finally, the novel polyurethane coating materials were prepared by the condensation polymerization of G- g -PLLA and isocyanate-terminated polyurethane prepolymer with polydimethylsiloxane. These synthesized materials were carefully analyzed with Fourier transform infrared spectroscopy (FTIR), proton nuclear magnetic resonance spectra ( 1 H NMR), field-emission scanning electron microscopy (SEM), and high-resolution transmission (TEM). In addition, the water contact angles were measured. It was found that the surface free energy of the polyurethane coating materials decreased from 52.19 to 11.74 N/m 2 with the increase of polydimethylsiloxane content from 0 to 20% and the water contact angle of the polyurethane coating materials increased from 71° to 108°. Moreover, the mechanical property was investigated. The studies also demonstrated that functionalized polyurethane was able to hydrolyze in seawater and the hydrolysis rate decreased as the PDMS content increased. At the same time, simulative ocean hanging plate experiment confirmed that the novel polyurethane coating materials exhibited a good antifouling performance, which indicated that the functionalized polyurethane has a potentiality in marine antifouling coating application.

• الناشر: Springer Berlin Heidelberg,Springer Nature B.V
• موضوع: Antifouling coatings / Biocompatibility / Characterization and Evaluation of Materials / Chemistry / Chemistry and Materials Science / Complex Fluids and Microfluidics / Condensation polymerization / Contact angle / Cycloaddition / Diphenyl methane diisocyanate / Emission spectra / Energy / Fourier transforms / Free energy / Graphene / Hydroxylation / Infrared analysis / Isocyanates / Mechanical properties / Nanoparticles / NMR / Nuclear magnetic resonance / Organic Chemistry / Original Paper / Physical Chemistry / Polydimethylsiloxane / Polylactic acid / Polymer Sciences / Polymerization / Polyurethane resins / Prepolymers / Protective coatings / Ring opening polymerization / Seawater / Soft and Granular Matter / Surface energy / Synthesis