Explore the vast range of titles available.

Chitin-nanofibrils are obtained in water suspension at low concentration, as nanoparticles normally are, to avoid their aggregation. The addition of the fibrils in molten PLA during extrusion is thus difficult and disadvantageous. In the present paper, the use of poly(ethylene glycol) (PEG) is proposed to prepare a solid pre-composite by water evaporation. The pre-composite is then added to PLA in the extruder to obtain transparent nanocomposites. The amount of PEG and chitin nanofibrils was varied in the nanocomposites to compare the reinforcement due to nanofibrils and plasticization due to the presence of PEG, as well as for extrapolating, where possible, the properties of reinforcement due to chitin nanofibrils exclusively. Thermal and morphological properties of nanocomposites were also investigated. This study concluded that chitin nanofibrils, added as reinforcing filler up to 12% by weight, do not alter the properties of the PLA based material; hence, this additive can be used in bioplastic items mainly exploiting its intrinsic anti-microbial and skin regenerating properties.

Environmental impacts and consumer concerns have necessitated the study of bio-based materials as alternatives to petrochemicals for packaging applications. The purpose of this review is to summarize synthetic and non-synthetic materials feasible for packaging and textile applications, routes of upscaling, (industrial) applications, evaluation of sustainability, and end-of-life options. The outlined bio-based materials include polylactic acid, polyethylene furanoate, polybutylene succinate, and non-synthetically produced polymers such as polyhydrodyalkanoate, cellulose, starch, proteins, lipids, and waxes. Further emphasis is placed on modification techniques (coating and surface modification), biocomposites, multilayers, and additives used to adjust properties especially for barriers to gas and moisture and to tune their biodegradability. Overall, this review provides a holistic view of bio-based packaging material including processing, and an evaluation of the sustainability of and options for recycling. Thus, this review contributes to increasing the knowledge of available sustainable bio-based packaging material and enhancing the transfer of scientific results into applications.

Poly(lactic acid) (PLA) was melt mixed in a laboratory extruder with poly(butylene adipate-co-terephthalate) (PBAT) and poly(butylene succinate) (PBS) in the presence of polypropylene glycol di glycidyl ether (EJ400) that acted as both plasticizer and compatibilizer. The process was then scaled up in a semi-industrial extruder preparing pellets having different content of a nucleating agent (LAK). All of the formulations could be processed by blowing extrusion and the obtained films showed mechanical properties dependent on the LAK content. In particular the tearing strength showed a maximum like trend in the investigated composition range. The films prepared with both kinds of blends showed a tensile strength in the range 12–24 MPa, an elongation at break in the range 150–260% and a significant crystallinity.

Chitin and lignin, by-products of fishery and plant biomass, can be converted to innovative high value bio- and eco-compatible materials. On the nanoscale, high antibacterial, anti-inflammatory, cicatrizing and anti-aging activity is obtained by controlling their crystalline structure and purity. Moreover, electropositive chitin nanofibrlis (CN) can be combined with electronegative nanolignin (NL) leading to microcapsule-like systems suitable for entrapping both hydrophilic and lipophilic molecules. The aim of this study was to provide morphological, physico-chemical, thermogravimetric and biological characterization of CN, NL, and CN-NL complexes, which were also loaded with glycyrrhetinic acid (GA) as a model of a bioactive molecule. CN-NL and CN-NL/GA were thermally stable up to 114 °C and 127 °C, respectively. The compounds were administered to in vitro cultures of human keratinocytes (HaCaT cells) and human mesenchymal stromal cells (hMSCs) for potential use in skin contact applications. Cell viability, cytokine expression and effects on hMSC multipotency were studied. For each component, CN, NL, CN-NL and CN-NL/GA, non-toxic concentrations towards HaCaT cells were identified. In the keratinocyte model, the proinflammatory cytokines IL-1α, IL-1 β, IL-6, IL-8 and TNF-α that resulted were downregulated, whereas the antimicrobial peptide human β defensin-2 was upregulated by CN-LN. The hMSCs were viable, and the use of these complexes did not modify the osteo-differentiation capability of these cells. The obtained findings demonstrate that these biocomponents are cytocompatible, show anti-inflammatory activity and may serve for the delivery of biomolecules for skin care and regeneration.

The present work focused on the research, design, and study of innovative chain extender systems of renewable origin for PLA–based biocomposites, reinforced with wheat bran as filler. The majority of employed chain extender compounds belongs to fossil world, affecting the biodegradability property which characterizes biopolymers. The aim of this work was thus to find promising biobased and sustainable alternatives to provide the same enhancements. According to this objective, epoxidized soybean oil (ESO) was chosen as principal component of the chain extender systems, together with a dicarboxylic acid, malic acid (MA), or succinic acid (SA). The reactivity of the modifier systems was previously studied through thermogravimetric analysis (TGA) and IR spectroscopy, to hypothesize the reaction mechanism in bran–filled blends. Hence, small–scale extrusion was carried out to investigate the effects of ESO/MA and ESO/SA on formulations of different composition (both pure PLA blends and composites). The variation of melt fluidity parameters was analyzed to define the optimized concentration of modifier systems. A comparison between the effects on blends of designed biobased systems and the action of fossil–based Joncryl was performed, to understand if the developed green solutions could represent competitive and efficient substitutes. The modified composites were characterized in terms of mechanical tests, degradation and thermal studies (TGA and DSC), and morphological analysis (SEM), to figure out their main features and to understand their potential in possible industrial applications.

In this work poly(lactic) acid (PLA)/poly(butylene succinate-co-adipate) (PBSA) biobased binary blends were investigated. PLA/PBSA mixtures with different compositions of PBSA (from 15 up to 40 wt.%) were produced by twin screw-extrusion. A first screening study was performed on these blends that were characterized from the melt fluidity, morphological and thermo-mechanical point of view. Starting from the obtained results, the effect of an epoxy oligomer (EO) (added at 2 wt.%) was further investigated. In this case a novel approach was introduced studying the micromechanical deformation processes by dilatometric uniaxial tensile tests, carried out with a videoextensometer. The characterization was then completed adopting the elasto-plastic fracture approach, by the measurement of the capability of the selected blends to absorb energy at a slow rate. The obtained results showed that EO acts as a good compatibilizer, improving the compatibility of the rubber phase into the PLA matrix. Dilatometric results showed different micromechanical responses for the 80–20 and 60–40 blends (probably linked to the different morphology). The 80–20 showed a cavitational behavior while the 60–40 a deviatoric one. It has been observed that while the addition of EO does not alter the micromechanical response of the 60–40 blend, it profoundly changes the response of the 80–20, that passed to a deviatoric behavior with the EO addition.

Poly(lactic acid)/poly(butylene succinate‐co‐adipate) (PLA/PBSA) blends are found promising for film packaging applications because of their flexibility, resistance, and compostability. Industrially extruded granules and films based on PLA and containing different amounts of PBSA are reprocessed through mini‐extrusion, to simulate recycling, and tested in terms of their melt flow rate as a function of PBSA content. Moreover, pure PLA commercial granules and the film produced extruding the PLA/PBSA 60/40 blend are reprocessed several times by injection molding and characterized in terms of melt flow rate, mechanical properties, thermal properties, and color as a function of injection molding cycles. The variation in melt fluidity and thermo‐mechanical properties is negligible up to 3 injection molding cycles for both pure PLA granules and PLA/PBSA blend. In the case of blend the change in color (yellowing and darkening) is more evident and slight local compositional change in injection molded items can be evidenced as well as a slight decrease in PBS crystallinity as a function of injection molding cycles. Nevertheless, in applications where these aspects are not critical, these materials can be recycled by extrusion or injection molding before being composted, thus prolonging their life cycle and storing carbon in them as longer as possible. The mechanical recyclability of Poly(lactic acid)/poly(butylene succinate‐co‐adipate) (PLA/PBSA) blends, which are found promising for film packaging applications, is investigated by extrusion or repeated injection molding. Despite some evidences of chain scission and yellowing, the results evidenced that these blends can be mechanically recycled before being composted, thus prolonging their life cycle and storing carbon in them as longer as possible.

The significant waste generated by the fashion industry necessitates sustainable textile recycling strategies. Polyester, made from poly(ethylene terephthalate) (PET), is abundant in post-consumer textiles. Technologies have been developed to convert low-density garment waste into flakes, but the role of color sorting in achieving uniform aesthetics in injection-moldable plastics remains underexplored. This study compares materials extruded from dark color-sorted polyester garment flakes with those from light-color flakes in terms of processability in extrusion and injection molding. The properties examined include melt fluidity, injection molding shrinkage, and mechanical and thermal properties. Commercial chain extenders with anhydride, oxazoline, or epoxide reactive groups were added during extrusion. Interestingly, only dark-colored extruded pellets showed significant degradation, but all the chain extenders allowed melt fluidity to be controlled during reprocessing. The bisoxazoline-based additive was the most promising, due to the highly improved ductility of the samples, regardless of whether they were dark-colored or light-colored. The results indicate significant potential for the industrial recycling of post-consumer textiles and highlight the industrial feasibility of repurposing post-consumer polyester garments. This approach not only supports initiatives of circular economy but also offers a viable solution for managing textile waste, particularly in the fashion industry. Additionally, the suggested recycling route combats the production of microplastics.

Biobased plastics are fully or partially made from biological resources but are not necessarily biodegradable or compostable. Poly (lactic acid) (PLA), one of the most diffused bioplastics, is compostable in industrial environments, but improving degradation in home composting conditions, in soil and in seawater could be beneficial for improving its end of life and general degradability. Blends obtained by the extrusion of PLA with different amounts of poly (butylene succinate-co-adipate) (PBSA) or poly (caprolactone) (PCL) were characterized in terms of their home composting, soil, marine and freshwater biodegradation. The blending strategy was found to be successful in improving the home compostability and soil compostability of PLA. Thanks to the correlations with morphological characterization as determined by electron microscopy, it was possible to show that attaining an almost co-continuous phase distribution, depending on the composition and melt viscosity of the blend components, can enhance PLA degradation in home composting conditions. Tests in marine and freshwater were also performed, and the obtained results showed that in marine conditions, pure PLA is degradable. A comparison of different tests evidenced that salt dissolved in marine water plays an important role in favoring PLA’s degradability.

Biodegradable polymers are promising materials for films and sheets used in many widely diffused applications like packaging, personal care products and sanitary products, where the synergy of high biocompatibility and reduced environmental impact can be particularly significant. Plasticized poly(lactic acid) (PLA)/poly(butylene succinate) (PBS) blend-based films, showing high cytocompatibility and improved flexibility than pure PLA, were prepared by laboratory extrusion and their processability was controlled by the use of a few percent of a commercial melt strength enhancer, based on acrylic copolymers and micro-calcium carbonate. The melt strength enhancer was also found effective in reducing the crystallinity of the films. The process was upscaled by producing flat die extruded films in which elongation at break and tear resistance were improved than pure PLA. The in vitro biocompatibility, investigated through the contact of flat die extruded films with cells, namely, keratinocytes and mesenchymal stromal cells, resulted improved with respect to low density polyethylene (LDPE). Moreover, the PLA-based materials were able to affect immunomodulatory behavior of cells and showed a slight indirect anti-microbial effect. These properties could be exploited in several applications, where the contact with skin and body is relevant.