Explore the vast range of titles available.

The sonication method was used to prepare a new set of CuO and CuO/Ag nanocomposites. The particle size was estimated using XRD and HR-TEM while the morphology of the nanoparticles was investigated with SEM. The average particle sizes of CuO and Ag falls in the 29.32–35.80 nm and 35.13–45.95 nm ranges, respectively. XRD declared that CuO has the space groups C 1 c 1 (9) and C 1 2/c 1 (15), while silver has space group F m -3 m (225). XPS analysis indicated the presence of Ag as Ag 0 and Cu as Cu 2+ . Nano-oxide and nanocomposites were used to synthesis CuO and CuO/Ag doped lithium–zinc borosilicate glass. Physical parameters of the glass samples were calculated including density, V m , V o , V m B , OPD, d B - B , n b , and N, R p , and R i depending on Ag and CuO mole fractions. The physical properties of glass indicated an increase in density and an initial expansion in glass structural network with the addition of silver metal due to its larger size followed by a compression as its molar ratio increase due to its higher C no . XRD measurements were reported for the glass samples doped with nanoparticles, proving the amorphous phase. ESR measurements were determined for all glass samples to detect the nature of the doped nanoparticles when incorporated inside a glassy matrix where CuO was found as tetragonal in octahedral sites and silver can be transformed after melting inside the glass matrix into Ag + to form more stable Ag y x + clusters.The fabricated sample of CuAgB-4 with significant nano silver doping (7.32% mol) has the maximum LAc and effective atomic number. Nano silver content increases the γ -RdSg in the lithium–zinc borosilicate glasses.

A new series of binary and ternary nanocomposites contains cobalt oxide or iron/cobalt oxides were manufactured to increase silicon dioxide shielding power. XRD indicated the presence of Co as Co 2.74 O 4 (COD: 1528446) and the presence of iron as Fe 3 O 4 (COD: 9002318 and 9005814). Using Profex, the Rietveld refinements were carried out. The R w , R ex , x 2 , and G of were 4.49, 4.34, 1.07, and 1.03, respectively, indicating good refinement parameters. XPS indicated the presence of Si ( ), Fe (Fe O ) and cobalt ( and ). TEM analysis showed that all metal oxide@SBA-15 solids have characteristic and well-organized SBA-15 structures. The -radiation shielding for the prepared samples were investigated via the Monte-Carlo code (MCN) and Phy-X software. The results confirmed that, adding high concentrations of cobalt-oxide and hematite increases the linear attenuation significantly. The SiCoFe-3 sample, which contains the highest content of cobalt-oxide and hematite, has the best -radiation shielding capability among all the synthesized SiCo/SiCoFe samples.

Background: Though acrylic resins possess many useful properties, denture fracture is nevertheless a familiar issue. Objective: This study aimed to determine the effect of low-percent recycled Zirconia nanoparticles as filler on the transverse strength, impact strength, surface hardness, water sorption, and solubility of resin using the sprinkle cold-curing technique. Materials and Methods: Various formulae were prepared and mixed with PMMA (polymer) powder containing varying percentages (0.01%, 0.1%, 0.3%, and 0.5%) of recycled Zr[O.sub.2]NPs to mono-methyl methacrylate (MMA monomer). A 2-hydroxyethylmethacrylate (HEMA) agent was used to functionalize recycled zirconia (Zr[O.sub.2]) nano-fillers. X-ray diffraction, field emission scanning electron microscopy, high-resolution transmission electron microscopy, energy-dispersive X-ray spectroscopy, and dynamic light scattering were used to characterize the samples. For mechanical tests, standard metallic moulds (according to American Dental Association specification no. 27) were machined for 60 specimens' preparation, 12 for each percent (zero, 0.01%, 0.1%, 0.3%, and 0.5%). A one-way ANOVA test was used to compare the five groups for parametric data, while the Kruskal-Wallis test was employed for nonparametric data. The P 0.05 value was accepted as the significance level. All formulae were tested for cytotoxicity at 24 and 48 hours on WI38 normal lung cell lines. Results: The XRD analysis demonstrated the tetragonal crystallographic structure of the recycled zirconia nanoparticles. Incorporating a low percentage of recycled Zr[O.sub.2] nanoparticles (0.01%, 0.1%, 0.3%, and 0.5%) improved the tested properties of PMMA to different degrees in a significant and non-significant pattern, while the optimal tested percent was 0.3%. Conclusion: The 0.3% percentage of recycled zirconia nanoparticles maintained and improved the physical and mechanical properties of acrylic resin. Recycled Zr[O.sub.2]/PMMA nanocomposite is a synergistic candidate due to its economic return and clinical application safety. Keywords: acrostone, cold cure, novel, recycled zirconia, sprinkle

Skin wound healing is one of the most challenging processes for skin reconstruction, especially after severe injuries. In our study, nanofiber membranes were prepared for wound healing using an electrospinning process, where the prepared nanofibers were made of different weight ratios of polycaprolactone and bioactive glass that can induce the growth of new tissue. The membranes showed smooth and uniform nanofibers with an average diameter of 118 nm. FTIR and XRD results indicated no chemical interactions of polycaprolactone and bioactive glass and an increase in polycaprolactone crystallinity by the incorporation of bioactive glass nanoparticles. Nanofibers containing 5% w/w of bioactive glass were selected to be loaded with atorvastatin, considering their best mechanical properties compared to the other prepared nanofibers (3, 10, and 20% w/w bioactive glass). Atorvastatin can speed up the tissue healing process, and it was loaded into the selected nanofibers using a dip-coating technique with ethyl cellulose as a coating polymer. The study of the in vitro drug release found that atorvastatin-loaded nanofibers with a 10% coating polymer revealed gradual drug release compared to the non-coated nanofibers and nanofibers coated with 5% ethyl cellulose. Integration of atorvastatin and bioactive glass with polycaprolactone nanofibers showed superior wound closure results in the human skin fibroblast cell line. The results from this study highlight the ability of polycaprolactone-bioactive glass-based fibers loaded with atorvastatin to stimulate skin wound healing.

Fabrications of nanomotors (NMs) are at the forefront of exploring the true potential of nanotechnology. Tubular nanomotors (TNMs) have been attracting huge interest recently. NMs based on 2D-hexagonal mesoporous silica (SBA-15) have been prepared through the surfactant-assisted sol–gel method. Copper and/or iron oxide nanoparticles have been impregnated in SBA-15 to form catalytic tubular nanomotors. Characterization has been investigated by XPS, XRD, HR-TEM, SEM–EDS, and BET. The electrochemical measurements were used to confirm the motion of the nanomotors. By increasing the loading of metal oxide nanoparticles, the motion decreases; this could be observed from the current loss. The anti-cancer potential of synthesized nanomotors against two cell lines (A549 and H460) of human lung carcinoma has been tested. Among all tested NMs, high-metal oxide-loaded materials containing CuO only as well as CuO and Fe 2 O 3 are potent and significant in apoptotic cell death for lung cancer treatment. Graphical abstract

A new series of binary and ternary nanocomposites contains cobalt oxide or iron/cobalt oxides were manufactured to increase silicon dioxide γ shielding power. XRD indicated the presence of Co as Co O (COD: 1528446) and the presence of iron as Fe O (COD: 9002318 and 9005814). Using Profex, the Rietveld refinements were carried out. The R , R , x , and G were 4.49, 4.34, 1.07, and 1.03, respectively, indicating good refinement parameters. XPS indicated the presence of Si ([Formula: see text]), Fe (Fe[Formula: see text]O[Formula: see text]) and cobalt ([Formula: see text] and [Formula: see text]). TEM analysis showed that all metal oxide@SBA-15 solids have characteristic and well-organized SBA-15 structures. The γ-radiation shielding for the prepared samples were investigated via the Monte-Carlo code (MCN) and Phy-X software. The results confirmed that, adding high concentrations of cobalt-oxide and hematite increases the linear attenuation significantly. The SiCoFe-3 sample, which contains the highest content of cobalt-oxide and hematite, has the best γ-radiation shielding capability among all the synthesized SiCo/SiCoFe samples.