Explore the vast range of titles available.

Lignocellulosic composites (LCs) were fabricated by partially dissolving cotton to create a matrix that was reinforced with osage orange wood (OOW) particles and/or blue agave fibers (AF). LCs were composed of 15–35% cotton matrix and 65–85% OWW/AF reinforcement. The matrix was produced by soaking cotton wool in a cold aqueous alkaline/urea solvent and was stirred for 15 minutes at 350 rpm to create a viscous gel. The gel was then reinforced with lignocellulosic components, mixed, and then pressed into a panel mold. LC panels were soaked in water to remove the aqueous solvent and then oven dried to obtain the final LC product. Several factors involved in the preparation of these LCs were examined including reaction temperatures (−5 to −15°C), matrix concentration (15–35% cotton), aqueous solvent volume (45–105 ml/panel), and the effectiveness of employing various aqueous solvent formulations. The mechanical properties of LCs were determined and reported. Conversion of the cotton into a suitable viscous gel was critical in order to obtain LCs that exhibited high mechanical properties. LCs with the highest mechanical properties were obtained when the cotton wools were subjected to a 4.6% LiOH/15% urea solvent at −12.5°C using an aqueous solvent volume of 60 ml/panel. Cotton wool subjected to excessive cold alkaline solvents volumes resulted in irreversible cellulose breakdown and a resultant LC that exhibited poor mechanical properties.

A systematic study of variables that affect the fiber welding process is presented. Cotton cloth samples are treated with controlled amounts of 1-ethyl-3-methylimidazolium acetate for a series of times and temperatures. Diluting the ionic liquid with a volatile molecular co-solvent allows temporal and spatial control of the welding process not possible with neat ionic liquids. Materials are characterized by scanning electron microscopy, infrared spectroscopy, X-ray diffraction, and mechanical (tensile) testing. Results suggest careful management of process variables permits controlled, reproducible manipulation of chemical and physical properties.

A technique was developed for preparing a novel material that consists of gold nanoparticles trapped within a fiber of unfolded proteins. These fibers are made in an aqueous solution that contains HAuCl 4 and the protein, bovine serum albumin (BSA). By changing the ratio of gold to BSA in solution, two different types of outcomes are observed. At lower gold to BSA ratios (30-120), a purple solution results after heating the mixture at 80 °C for 4 h. At higher gold to BSA ratios (130-170), a clear solution containing purple fibers results after heating the mixture at 80 °C for 4 h. UV-Vis spectroscopy and light scattering techniques show growth in nanocolloid size as gold to BSA ratio rises above 100. Data indicate that, for the higher gold to BSA ratios, the gold is sequestered within the solid material. The material mass, visible by eye, appears to be an aggregation of smaller individual fibers. Scanning electron microscopy and transmission electron microscopy indicate that these fibers are primarily one-dimensional aggregates, which can display some branching, and can be as narrow as 400 nm in size. The likely mechanism for the synthesis of the novel material is discussed.

A technique was developed for preparing a novel material that consists of gold nanoparticles trapped within a fiber of unfolded proteins. These fibers are made in an aqueous solution that contains HAuCl and the protein, bovine serum albumin (BSA). By changing the ratio of gold to BSA in solution, two different types of outcomes are observed. At lower gold to BSA ratios (30-120), a purple solution results after heating the mixture at 80 °C for 4 h. At higher gold to BSA ratios (130-170), a clear solution containing purple fibers results after heating the mixture at 80 °C for 4 h. UV-Vis spectroscopy and light scattering techniques show growth in nanocolloid size as gold to BSA ratio rises above 100. Data indicate that, for the higher gold to BSA ratios, the gold is sequestered within the solid material. The material mass, visible by eye, appears to be an aggregation of smaller individual fibers. Scanning electron microscopy and transmission electron microscopy indicate that these fibers are primarily one-dimensional aggregates, which can display some branching, and can be as narrow as 400 nm in size. The likely mechanism for the synthesis of the novel material is discussed.