Explore the vast range of titles available.

The microstructure evolution and impact-toughness variation of heat-affected zone（HAZ）in X80 highstrain pipeline steel were investigated via a welding thermal-simulation technique,Charpy impact tests,and scanning electron microscopy observations under different welding heat inputs and peak temperatures.The results indicate that when heat input was between 17 and 25kJ·cm~（-1）,the coarse-grained heat-affected zone showed improved impact toughness.When the heat input was increased further,the martensite-austenite（M-A）islands transformed from fine lath into a massive block.Therefore,impact toughness was substantially reduced.When the heat input was 20kJ·cm~（-1） and the peak temperature of the first thermal cycle was between 900 and 1300°C,a higher impact toughness was obtained.When heat input was 20kJ·cm~（-1） and the peak temperature of the first thermal cycle was 1300°C,the impact toughness value at the second peak temperature of 900°C was higher than that at the second peak temperature of 800°C because of grain refining and uniformly dispersed M-A constituents in the matrix of bainite.

A new ultrahigh strength pipeline steel with high yield strength and high impact toughness was fabricated in this work, and mechanical properties and microstructure of the steel were investigated. The steel exhibited out- standing mechanical properties with yield strength levels of up to 951 MPa and tensile strength levels up to 1023 MPa. The sharp notch toughness with absorbed energy values of 227 J/cm2 at -30℃ and shear area of up to 95% in drop weight tear test （DWTT） at temperature of --20℃ were achieved. It was found that microstructure of the steel com- prises a majority of low-carbon lath bainite with different sublaths and sub-sublaths, meanwhile there is a high density of dislocation between laths and the dispersed film-like martensite-austenite （M-A） constituents. Most of the precipi- tates in this steel are duplex type containing Nb and Ti with characterized morphology of cap with the range of precipitation size from a few to tens nanometers.

Effect of boron on the microstructure and impact toughness in the coarse-grained heat-affected zone（CGHAZ）of two high strength low alloy steels,boron-free and boron-containing,was investigated by means of weld thermal simulation test.The result shows that,for the boron-free steel,a microstructure consisting of grain boundary ferrite degenerates pearlite and granular bainite for longer t8/5（the cooling time from 800 to 500 ℃）,while lath bainite for shorter t8/5.For the boron-containing steel,granular bainite is dominant for a wide range of t8/5.Continuous cooling transformation（CCT）study on the CGHAZ indicates that the transformation start temperature decreases by about 50-100℃under different t8/5,for the boron-containing steel compared with the boron-free steel.The presence of boron suppresses the nucleation of ferrite at prior austenite grain boundaries and hence enlarges the range of t8/5for granular bainite transformation.However,the addition of boron deteriorates the impact toughness of CGHAZ,which may be due to a markedly increased fraction of martensite-austenite（M-A）constituents and decreased fraction of high angle grain boundaries.

The microstructure and mechanical properties of low carbon bainite high strength steel plate were studied via different cooling paths at the pilot scale. There was a significant increase in mechanical properties, and notably, the yield strength, tensile strength, and toughness at-40 ℃ for the tested steel processed by ultra-fast cooling were 126 MPa, 98 MPa and 69 J, respectively, in relation to steel processed by accelerated cooling. The ultra-fast cooling rate not only refined the microstructure, precipitates, and martensiteaustenite（M/A） islands, but also contributed to the refinement of microstructure in thick plates. The large size M/A constituents formed at lower cooling rate experienced stress concentration and were potential sites for crack initiation, which led to deterioration of low-temperature impact toughness. In contrast, the acicular ferrite and lath bainite with high fraction of high-angle grain boundaries were formed in steel processed by ultra-fast cooling, which retarded cleavage crack propagation.

The impact toughness of EN-GJS-400-18-LT ductile iron was measured by Charpy V-notch impact test at temperature between-80 and 20℃.The fracture properties were tested under instrumented impact loading.Total impact fracture energy,crack initiation and propagation energy,dynamic loads and the ductile to brittle temperature were measured.Three-dimensional reconstruction of impact fracture morphology was accomplished by confocal laser scanning microscope.The results of quantitative fractography indicate that cleavage fracture produces flatter fracture surfaces accompanying with less absorbed energy during the impact fracture process.It indicates that fracture roughness has a close relationship with crack propagation energy at low temperature.

The influence of Nb on microstructure, mechanical property and the transformation kinetics of the coarse grain heat affected zone （CGHAZ） in HSLA steels for different heat inputs, has been investigated. When welded at higher heat inputs （100-60 kJ/cm）, impact toughness values of the steel without Nb are much higher than those of the steel with Nb, and the lowest span is 153 J at 60 kJ/cm. But only a little higher values are observed at lower heat inputs （40-30 kJ/cm）, and the highest span is 68 J at 30 kJ/cm. Dilatation studies indicate that continuous cooling transformation starting temperatures （Ts） of CGHAZ for the steel with Nb are approximately 15-30℃ which are lower than those of the steel without Nb at all heat inputs. For higher heat inputs, Nb in solid solution suppresses ferrite transformation and promotes the formation of granular bainite which has detrimental effect on impact toughness. For lower heat inputs higher Charpy impact energy values in the steel with Nb are associated with the formation of low carbon self-tempered martensite.

The effects of Ni content and heat-treatment process on the toughness of a super ferritic stainless steel with 26 wt% Cr and 3.5 wt% Mo were investigated. It was found that with the increase of Ni content, the Charpy impact toughness improved remarkably, and transformed from cleavage brittle fracture to the most ductile fracture. There were no obvious differences between the high- and low-Ni contents on the microstructure and mechanical properties since the addition of Ni did not influence crystal structure, phase composition, and precipitation of ultra pure ferritic stainless steels. Meanwhile, the heat-treatment process was a key point to maintain a high level of toughness by optimizing structure and removing detrimental precipitation, i.e., chi phase.

The as-cast microstructure of H13 ESR ingot and the influence of high temperature diffusion treatment on the structure and impact toughness have been investigated. The results show that the dendrite arm spacing gradually becomes wide from the surface to the center of ingot, and the large primary carbide particles always exist in interdendritic segregation areas; by means of high temperature diffusion treatment of ingot prior to hot forging, the banded segregation is nearly eliminated, the annealed structure is more uniform and the isotropic properties have been improved remarkably.

The impact toughness scattering in the ductile-brittle transition temperature （DBTT） region was experimentally examined on mixed and homogeneous grains of low alloy high strength bainitic steel under dynamic loading conditions. The results revealed that the mixed grain microstructure had larger impact toughness scattering than the homogeneous one, and the impact toughness scattering was mainly caused by the scattering in the cleavage fractttre stress σf. The value of σf. is related to the size of the microcrack formed in the bainitic packet. When a bainitic packet-sized microcrack propagates from one bainitic packet into the adjacent packet, cleavage fracture occurs. The cleavage fracture is controlled by the few coarse packets in the microstructures, and the σf scattering is influenced by the varied distances/relative locations between these coarse packets, and homogenizing the distribution of fine bainitic packet sizes is an effective way to reduce the impact toughness scattering in the DBTT region.

The microstructure analysis and mechanical properties evaluation of laser beam welded AISI 409M ferritic stainless steel joints are investigated. Single pass autogeneous welds free of volumetric defects were produced at a welding speed of 3 000 mm/min. The joints were subjected to optical microscope, scanning electron fractographe, microhardness, transverse and longitudinal tensile, bend and charpy impact toughness testing. The coarse ferrite grains in the base metal were changed into dendritic grains as a result of rapid solidification of laser beam welds. Tensile testing indicates overmatching of the weld metal is relative to the base metal. The joints also exhibited acceptable impact toughness and bend strength properties.