Asset Details
Do you wish to reserve the book?
Effect of As-Rolled Microstructure on Static Recrystallization Characteristics and Texture Evolution during Annealing
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Effect of As-Rolled Microstructure on Static Recrystallization Characteristics and Texture Evolution during Annealing
Do you wish to request the book?
Effect of As-Rolled Microstructure on Static Recrystallization Characteristics and Texture Evolution during Annealing
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Effect of As-Rolled Microstructure on Static Recrystallization Characteristics and Texture Evolution during Annealing
2017
Overview
Magnesium AZ31 alloy sheets were rolled at 100 °C at a high rolling speed of 1000 m/min. After 30% reduction, the microstructure was heavily twinned and shear banded, while a partially dynamically recrystallized and twinned microstructure was seen at the reduction of 49%. The as-rolled specimens were then annealed at 500 °C for increasing times. Microstructure and texture were characterized by optical microscopy, electron backscattered diffraction (EBSD) and X-ray diffraction (XRD). Texture weakening was found during annealing of the specimens at both reductions. However, the texture weakening was more effective in the fully twinned and shear banded specimen than the partially DRXed and twinned specimen. Effects of as-rolled microstructure on static recrystallization characteristics and texture evolution during annealing were studied.