Asset Details
Do you wish to reserve the book?
The fracture properties of a smart fiber metal laminate
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
The fracture properties of a smart fiber metal laminate
Do you wish to request the book?
The fracture properties of a smart fiber metal laminate
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
The fracture properties of a smart fiber metal laminate
2007
Overview
This paper investigates the interfacial, tensile, and fatigue properties of a novel smart fiber‐metal laminate (FML) based on a nickel‐titanium (Ni‐Ti) shape memory alloy and a woven glass fiber reinforced epoxy. Initial tests, using the single cantilever beam (SCB) geometry, have shown that this unique system offers high values of metal‐composite interfacial fracture toughness. Tensile tests have shown that the mechanical properties of these FMLs lie between those offered by its constituent materials and that their tensile modulus and strength can be easily predicted using a rule of mixtures approach. Tension‐tension fatigue tests have shown that the fatigue performance of notched smart FMLs is superior to that offered by the plain Ni‐Ti alloy. A subsequent optical examination of unnotched laminates tested to failure under tension‐tension fatigue loading has shown that the fracture mechanisms occurring within the Ni‐Ti FMLs are strongly dependent on the applied cyclic stress. POLYM. COMPOS., 28:534–544, 2007. © 2007 Society of Plastics Engineers