Asset Details
Do you wish to reserve the book?
Influence of Pitting Corrosion on TIG Welded Joints of AA2024 Aluminum Alloy Joints
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Influence of Pitting Corrosion on TIG Welded Joints of AA2024 Aluminum Alloy Joints
Do you wish to request the book?
Influence of Pitting Corrosion on TIG Welded Joints of AA2024 Aluminum Alloy Joints
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Influence of Pitting Corrosion on TIG Welded Joints of AA2024 Aluminum Alloy Joints
2021
Overview
In this investigation, AA2024 alloy was welded by tungsten inert gas welding. Access the influence of pitting corrosion on TIG weld; the joints were heat-treated after welding with different techniques. Moreover, the corrosion test was carried out with 3.5% NaCl solution under different pH values such as pH:5, pH:7, and pH: 12. From the experimental results, the joint treated with solution treatment with pH: 7 showed high corrosion resistance than its counterparts.