Asset Details
Do you wish to reserve the book?
Effect of Mg/Al2O3 and Calcination Temperature on the Catalytic Decomposition of HFC-134a
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Effect of Mg/Al2O3 and Calcination Temperature on the Catalytic Decomposition of HFC-134a
Do you wish to request the book?
Effect of Mg/Al2O3 and Calcination Temperature on the Catalytic Decomposition of HFC-134a
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Effect of Mg/Al2O3 and Calcination Temperature on the Catalytic Decomposition of HFC-134a
2019
Overview
This paper evaluated the effect of calcination temperature and the use of Mg/Al2O3 on the decomposition of HFC-134a. Two commercialized catalysts, Al2O3 and Mg/Al2O3, were calcined at two different temperatures (500 and 650 °C) and their physicochemical characteristics were examined by X-ray diffraction, Brunauer–Emmett–Teller analysis, and the temperature-programed desorption of ammonia and carbon dioxide analysis. The results show that, in comparison to Al2O3, 5% Mg/Al2O3 exhibited a larger Brunauer–Emmett–Teller surface area and higher acidity. The relative amount of strong acid sites of the catalysts decreased with increasing calcination temperature. Although a more than 90% decomposition rate of HFC-134a was achieved over all catalysts during the sequential decomposition test of HFC-134a using a vertical plug flow reactor connected directly to a gas chromatography/mass spectrometry system, the lifetime of the catalyst differed according to the catalyst type. Compared to Al2O3, Mg/Al2O3 revealed a longer lifetime and less coke formation due to the increased Brunauer–Emmett–Teller surface area and weak Lewis acid sites and basic sites arising from Mg impregnation. Higher temperature calcination extended the catalyst lifetime with the formation of less coke due to the smaller number of strong acid sites, which can lead to severe coke formation. A valuable by-product, trifluoroethylene, was formed as a result of the decomposition. Based on the experimental results, a reaction is proposed which reasonably explains the decomposition reaction.