Asset Details
Do you wish to reserve the book?
Development of New Device and Process to Recover Valuable Materials from Spent Solar Module
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Development of New Device and Process to Recover Valuable Materials from Spent Solar Module
Do you wish to request the book?
Development of New Device and Process to Recover Valuable Materials from Spent Solar Module
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Development of New Device and Process to Recover Valuable Materials from Spent Solar Module
2018
Overview
As industry enters into high-tech society, the use of fossil energies is increasing. The demand of solar photovoltaic cell is increasing and according to this increase, the amount of waste photovoltaic cell will increase, too. However, compared to the increase of photovoltaic facility and technology, research about recycling method of waste photovoltaic cell is slow. Therefore, this study continued research to collect cooper and tin which are valuable metals from cooper ribbon electrode recovered from waste photovoltaic electrode. To effectively separate the coating layer when handling bulk of cooper ribbon electrode, heat treating furnace of hydrodynamic vibrating is developed and tin and cooper which are valuable metals are collected by using Hydro-metallurgical process used with nitric acid. The purity of cooper’s basic materials after heat treatment of hydrodynamic vibrating was 98.88wt.% and the purity of tin and cooper collected from the coating layer was measured as 98.07wt.% and 98.44wt.% each.