Asset Details
Do you wish to reserve the book?
Bending performance of sandwich flooring with wood exterior and two-layer cork interior reinforced separately with metal, glass fiber, or carbon fiber
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Bending performance of sandwich flooring with wood exterior and two-layer cork interior reinforced separately with metal, glass fiber, or carbon fiber
Do you wish to request the book?
Bending performance of sandwich flooring with wood exterior and two-layer cork interior reinforced separately with metal, glass fiber, or carbon fiber
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Bending performance of sandwich flooring with wood exterior and two-layer cork interior reinforced separately with metal, glass fiber, or carbon fiber
2025
Overview
To expand the potential of cork composite wood flooring as an interior material, this study investigated the bending performance of sandwich-structured cork composite wood flooring. The cork composite wood flooring was composed of temperate and tropical wood species as face layer and a cork board reinforced with metal, glass fiber, or carbon fiber placed between two cork boards as the core layer. The MOE value of wood flooring with merbau (M) had the highest value (6.71 GPa) and that of larch (La) had the lowest value (5.40 GPa). Overall, the MOE value of wood flooring with tropical wood species had higher value than those with temperate wood species, which had lower densities. According to the core reinforcements, the CM (cork board-metal) type showed a higher MOE value than the CG (cork board-glass fiber) and CC (cork board-carbon fiber) types. However, within the specific MOE, the order was CG > CC > CM. The ratio measured to calculated MOE ranged from 1.0 to 1.1, it showed a similar or slightly higher value than the measured MOE. The MOR of wood flooring had the highest value (51.0 MPa) in that with teak (T) and had the lowest value (34.9 MPa) in that with larch (La). The specific MOR of the wood floorings with cork board reinforced with glass fiber and carbon fiber was 20 to 40% higher than those reinforced with metal. Stable fracture behavior was observed for the cork composite wood flooring reinforced with metal, glass fiber, or carbon fiber.