Asset Details
Do you wish to reserve the book?
Microstructure Evolution and Mechanical Properties of a Directionally Solidified Nb-Ti-Si-Cr-Al-Hf-Dy Alloy
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Microstructure Evolution and Mechanical Properties of a Directionally Solidified Nb-Ti-Si-Cr-Al-Hf-Dy Alloy
Do you wish to request the book?
Microstructure Evolution and Mechanical Properties of a Directionally Solidified Nb-Ti-Si-Cr-Al-Hf-Dy Alloy
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Microstructure Evolution and Mechanical Properties of a Directionally Solidified Nb-Ti-Si-Cr-Al-Hf-Dy Alloy
2016
Overview
The Nb-Ti-Si-Cr-Al-Hf-Dy alloy was prepared by conventionally casting and then directionally solidified (DS) with the optical floating zone melting technology. Microstructural evolution and mechanical properties of the as cast (AC) and DS alloys were studied by XRD, SEM, TEM, compression and bending tests. The results exhibit that α-(Nb, Ti)5Si3, (Ti, Nb)5Si3 and (Nb, Ti)ss phases formed the microstructure of the AC alloy, with precipitates of Cr2Nb, Dy2O3 and (Nb, Ti)3Si along phase or grain boundaries. The DS alignes (Nb, Ti)ss and α-(Nb, Ti)5Si3 lamellae parallel to the growth direction and refines the eutectic cell, but coarsens the primary α-(Nb, Ti)5Si3 phase. The DS alloy exhibits strong orientation of (310)(Nb, Ti)5Si3 and (110)(Nb, Ti)ss along the growth direction. TEM observation reveals that (Nb, Ti)ss and α-(Nb, Ti)5Si3 phases have an orientation relationship of [110](Nb, Ti)ss // [310]α-(Nb, Ti)5Si3 and (002)(Nb, Ti)ss // (002)α-(Nb, Ti)5Si3. Compared with the AC alloy, the DS increases the mechanical properties of the alloy obviously and the alloy DS at 8 mm/h exhibits the best mechanical properties.
Publisher
EDP Sciences