Asset Details
Do you wish to reserve the book?
Mechanical Properties of the Cured Laminates on the Hot-press Tackified Preforms in Vacuum Assisted Resin Transfer Molding
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Mechanical Properties of the Cured Laminates on the Hot-press Tackified Preforms in Vacuum Assisted Resin Transfer Molding
Do you wish to request the book?
Mechanical Properties of the Cured Laminates on the Hot-press Tackified Preforms in Vacuum Assisted Resin Transfer Molding
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Mechanical Properties of the Cured Laminates on the Hot-press Tackified Preforms in Vacuum Assisted Resin Transfer Molding
2018
Overview
A hot-press tackified preform was used to improve the uniformity of the laminates thickness and the mechanical properties of the obtained laminates were studied using vacuum assisted resin transfer molding（VARTM）. Two modified preforms were prepared under 0.1 and 0.6 MPa in an autoclave and then were used to fabricate the laminates via VARTM. Permeability and thickness distribution of the laminates were obtained by using a special device. Moreover, the tensile and compressive strengths of the obtained laminates were studied and compared with the unmodified ones. Results show that the tackified laminates present a maximum and minimum thickness under 0.1 and 0.6 MPa, respectively. The thicknesses and in-plane permeability of the tackified laminates, with better thickness uniformity, are significantly decreased compared with that of the unmodified cases, while the tensile and compressive strengths of the tackified laminates are improved obviously. Results show that the mechanical property of the tackified laminates prepared by hotpressing at 0.1 MPa is better than that processed at 0.6 MPa.
Publisher
Wuhan University of Technology,Springer Nature B.V