Asset Details
Do you wish to reserve the book?
Transport and Durability Properties of Alkali-Activated Natural Pozzolan/Slag Concrete
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Transport and Durability Properties of Alkali-Activated Natural Pozzolan/Slag Concrete
Do you wish to request the book?
Transport and Durability Properties of Alkali-Activated Natural Pozzolan/Slag Concrete
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Transport and Durability Properties of Alkali-Activated Natural Pozzolan/Slag Concrete
2019
Overview
The current study aims to assess the transport and durability properties of alkali-activated concretes made with hybrid aluminosilicate precursors having different proportions of natural pozzolan as a low-calcium precursor and ground-granulated blastfurnace slag as a high-calcium precursor, which are activated with different concentrations and combinations of sodium hydroxide and sodium silicate. The studied parameters included precursor combination (natural pozzolan'slag combinations of 30/70, 50/50, and 70/30), sodium hydroxide concentration (1, 1.75, and 2.5 M), and activator combination (sodium hydroxide/sodium silicate combinations of 70/30, 75/25, and 80/20). The resulting concrete mixtures were tested for slump flow, setting time, compressive strength, absorption, rapid chloride penetration, rapid chloride migration, resistance to sulfuric acid attack, chloride-induced corrosion, and frost resistance. Mercury intrusion porosimetry and X-ray diffraction were used to justify the observed behaviors. The performance of alkali-activated natural pozzolan/slag concretes was also compared with that of a reference concrete made with solely portland cement binder. In view of overall performance, an equal proportion of natural pozzolan and slag (50/50) and a 30/70 combination of sodium silicate and sodium hydroxide proved to be the optimum precursor and activator combinations. The optimum sodium hydroxide concentration was dependent on the precursor and activator combinations as well as the expected fresh, strength, transport and durability performance. In terms of the measured transport properties (that is, absorption, chloride penetration depth, and passing charges) and resistance to acid attack and chloride-induced corrosion, all the studied alkali-activated concretes performed considerably superior to the reference portland cement concrete. In the case of frost resistance, only alkali-activated concretes with 50 and 70% slag performed superior to the reference portland cement concrete. Keywords: acid attack; activator combination; alkali activation; corrosion; frost resistance; natural pozzolan; precursor combination; slag; sodium hydroxide concentration; transport properties.