Effect of Two Steps Overaging on Mechanical Properties of Tailor Rolled Blank of Dual Phase Steel

Zhi, Ying, Ke, Diwen, Hu, Xianlei, Liu, Xianghua

2021

Overview

Herein, a new kind of overaging strategy: two steps of overaging for tailor rolled blank of dual phase steel (DP-TRB) was investigated. The results indicate that two steps of the overaging process is a useful way to control the mechanical properties of DP-TRB. In the premise of satisfying the requirement for the strength of DP590 grade, the total elongation can be significantly increased (3~7% in most cases). Due to the different degrees of ferrite recrystallization (differences of densities of dislocation) among the thicknesses, the obvious changes of mechanical properties among thicknesses are found. The thicknesses zones of 1.0~1.4 mm show lower strength, while the zones of 1.6~1.8 mm present higher strength. Otherwise, the high density of dislocations in samples of 1.6~1.8 mm provide more locations for Cottrell atmospheres, yield plateau occur easier. The zones with different thicknesses for one DP-TRB show two kinds of yield behaviors (continuous yield and non-continuous yield) simultaneously. The subtle C diffusion control by two step overaging leads to the quite different pinning effect of Cottrell atmospheres. Thus, the pinning effect occurs in a gradual way, and a transition state of yield behavior, which combines the characteristic of smooth curve in continuous yield and the plateau in non-continuous yield, is found.

• Publisher: MDPI AG
• Subject: Annealing / Atmospheres / Decomposition / Dislocation density / dual phase steel / Dual phase steels / Ductility / Elongation / Mechanical properties / Overaging / overaging process / Raw materials / Recrystallization / Steel products / tailor rolled blank / Tension tests / Thickness