Asset Details
Do you wish to reserve the book?
Microstructure and Its Influence on the Welding Quality of 6063 Aluminum Alloy Porthole Die Extrusion
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Microstructure and Its Influence on the Welding Quality of 6063 Aluminum Alloy Porthole Die Extrusion
Do you wish to request the book?
Microstructure and Its Influence on the Welding Quality of 6063 Aluminum Alloy Porthole Die Extrusion
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Microstructure and Its Influence on the Welding Quality of 6063 Aluminum Alloy Porthole Die Extrusion
2021
Overview
Extrusion experiments and 3D numerical modeling were conducted to investigate the dynamic recrystallization and welding quality of a 6063 aluminum alloy hollow square tube extruded by a porthole die at the ram speeds of 3 mm/s, 7 mm/s, 9 mm/s and 11 mm/s. The results showed that average grain size of hollow square tube extruded at the ram speed of 7 mm/s was the smallest. The profile extruded at the ram speed of 3 mm/s exhibited the highest expansion ratio. Dynamic recrystallization (DRX) fractions were highly variable at different ram speeds. DRX fractions in the matrix zones were higher than those in the welding zones, resulting in smaller grain sizes in the matrix zones. Mechanical properties in the welding zones and matrix zones was different. A local strain concentration would occurred during expansion, which would affect the welding quality. Finally, it was found that the uniform microstructure near the welding line would also affect the welding quality.
Publisher
MDPI AG,MDPI