Influence of Oxygen Diffusion on Thermal Ageing of Cross-Linked Polyethylene Cable Insulation
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Influence of Oxygen Diffusion on Thermal Ageing of Cross-Linked Polyethylene Cable Insulation
Do you wish to request the book?
Influence of Oxygen Diffusion on Thermal Ageing of Cross-Linked Polyethylene Cable Insulation
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Influence of Oxygen Diffusion on Thermal Ageing of Cross-Linked Polyethylene Cable Insulation
2020
Overview
Thermal ageing of cross-linked polyethylene (XLPE) cable insulation is an important issue threatening the safe operation of power cables. In this paper, thermal ageing of XLPE was carried out at 160 °C in air for 240 h. The influence of oxygen diffusion on thermal ageing of XLPE was investigated by Ultraviolet–visible spectrophotometer (UV–Vis), tensile testing, and Fourier transformed infrared spectroscopy (FTIR). It was observed that the degradation degree not only depended on ageing time but also on sample positions. The thermally aged samples were more oxidized in the surface region, presented a darker color, more carbon atoms appeared in the conjugate cluster, had smaller elongation at break and tensile strength, and a larger carbonyl index. As ageing time increased, the non-uniform oxidation of the XLPE samples became more prominent. The degree of non-uniform oxidation caused by oxygen diffusion was quantitatively studied by first order oxidation kinetic. The calculated results demonstrated that carbonyl index measured by FTIR was more sensitive to non-uniform oxidation with a shape parameter in the range of 1–2. The result shown in this paper is helpful for interpreting and predicting the non-uniform ageing behavior of high voltage XLPE cables.