Asset Details
Do you wish to reserve the book?
Phase Evaluation, Mechanical Properties and Thermal Behavior of Hot-Pressed LC-YSZ Composites for TBC Applications
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Phase Evaluation, Mechanical Properties and Thermal Behavior of Hot-Pressed LC-YSZ Composites for TBC Applications
Do you wish to request the book?
Phase Evaluation, Mechanical Properties and Thermal Behavior of Hot-Pressed LC-YSZ Composites for TBC Applications
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Phase Evaluation, Mechanical Properties and Thermal Behavior of Hot-Pressed LC-YSZ Composites for TBC Applications
2022
Overview
In this work, La2Ce2O7-yttria-stabilized zirconia (LC-YSZ) composites with different weight fractions of YSZ (40–70 wt.%) were prepared by hot pressing at 1400 °C and investigated as a material for thermal barrier-coating (TBC) applications. For this purpose, the effect of YSZ addition on the phase composition, microstructure, mechanical performance and thermal behavior was studied. X-ray diffraction analysis showed that the LC-YSZ composites were mainly composed of a cubic ZrO2 and La2O3-CeO2-ZrO2 solid solution with a pyrochlore structure, indicating that the reaction between LC and YSZ took place during hot pressing. Scanning electron microscopy revealed the high microstructural stability of the prepared composites, as the pore formation was significantly controlled and a high relative density (>97%) was obtained. The microstructure of LC-YSZ bulk samples was relatively fine-grained, with an average grain size below or very close to 1 µm. YSZ doping improved the Vickers hardness of the LC-YSZ composites; the highest hardness, with value of 12 ± 0.62 GPa, was achieved for the composite containing 70 wt.% of YSZ. The fracture toughness of LC-YSZ composites was in the range from 2.13 to 2.5 MPa·m1/2. No statistically significant difference in heat capacity or thermal conductivity was found between the composites with different content of YSZ. The results showed that LC-YSZ composites have relatively low thermal conductivities from room temperature (1.5–1.8 W·m−1·K−1) up to 1000 °C (2.5–3.0 W·m−1·K−1). This indicates that the prepared LC-YSZ composite materials are promising candidates for TBC applications.
Publisher
MDPI AG,MDPI
Subject
/ Graphite