Asset Details
Do you wish to reserve the book?
Highly Productive Laser Annealing Manufacturing Method Using Continuous Blue WBC (Wavelength Beam Combining) Technique
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Highly Productive Laser Annealing Manufacturing Method Using Continuous Blue WBC (Wavelength Beam Combining) Technique
Do you wish to request the book?
Highly Productive Laser Annealing Manufacturing Method Using Continuous Blue WBC (Wavelength Beam Combining) Technique
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Highly Productive Laser Annealing Manufacturing Method Using Continuous Blue WBC (Wavelength Beam Combining) Technique
2024
Overview
Blue laser annealing can be used to obtain a high-mobility thin-film transistor (TFT) through a laser annealing (i.e., LTPS: low-temperature Poly-Si) process. However, the laser annealing process’s low productivity (as well as high cost) is an issue because the high output power of blue lasers still needs to be addressed. Therefore, productivity can be improved if blue laser energy is efficiently supplied during the laser annealing process using a continuous wave laser instead of a conventional pulsed excimer laser. We developed a blue laser light source (440 ± 10 nm) using the wavelength beam combining (WBC) method, which can achieve a laser power density of 73.7 kW/cm2. In this semiconductor laser, when the power was increased s by 2.9 times, the laser scanning speed was increased by 5.0 times, achieving twice the productivity of conventional lasers. After laser annealing, the size of the crystal grains varied between 2 and 15 μm, resulting in a crystallization rate of 100% by Raman scattering rsult and low resistivity of 0.04 Ωcm. This increase in production capacity is not an arithmetic increase with increased power but a geometric production progression.