Asset Details
Do you wish to reserve the book?
Evolution of Grain Boundary Character Distribution in B10 Alloy from Friction Stir Processing to Annealing Treatment
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Evolution of Grain Boundary Character Distribution in B10 Alloy from Friction Stir Processing to Annealing Treatment
Do you wish to request the book?
Evolution of Grain Boundary Character Distribution in B10 Alloy from Friction Stir Processing to Annealing Treatment
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Evolution of Grain Boundary Character Distribution in B10 Alloy from Friction Stir Processing to Annealing Treatment
2024
Overview
In this study, the grain boundary character distribution (GBCD) of a B10 alloy was optimized, employing thermomechanical processing consisting of friction stirring processing (FSP) and annealing treatment. Using electron backscatter diffraction, the effects of rotational speed of FSP and annealing time on the evolution of GBCD were systematically investigated. The GBCD evolution was analyzed concerning various parameters, such as the fraction of low-Σ coincidence site lattice (CSL) boundaries, the average number of grains per twin-related domain (TRD), the length of longest chain (LLC), and the triple junction distribution. The experimental results revealed that the processing of a 1400 rpm rotational speed of FSP followed by annealing at 750 °C for 60 min resulted in the optimum grain boundary engineering (GBE) microstructure with the highest fraction of low-Σ CSL boundaries being 82.50% and a significantly fragmented random boundary network, as corroborated by the highest average number of grains per TRD (14.73) with the maximum LLC (2.14) as well as the highest J2/(1 − J3) value (12.76%). As the rotational speed of FSP increased from 600 rpm to 1400 rpm, the fraction of low-Σ CSL boundaries monotonously increased. The fraction of low-Σ CSL boundaries first increased and then decreased with an increase in annealing time. The key to achieving GBE lies in inhibiting the recrystallization phenomenon while stimulating abundant multiple twinning events through strain-induced boundary migration.