Asset Details
Do you wish to reserve the book?
Effect of Exposure Environment and Calcium Source on the Biologically Induced Self-Healing Phenomenon in a Cement-Based Material
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Effect of Exposure Environment and Calcium Source on the Biologically Induced Self-Healing Phenomenon in a Cement-Based Material
Do you wish to request the book?
Effect of Exposure Environment and Calcium Source on the Biologically Induced Self-Healing Phenomenon in a Cement-Based Material
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Effect of Exposure Environment and Calcium Source on the Biologically Induced Self-Healing Phenomenon in a Cement-Based Material
2024
Overview
Microbially induced calcium carbonate precipitation (MICP) presents a sustainable, environmentally friendly solution for repairing cracks in cement-based materials, such as mortar and concrete. This self-healing approach mechanism enables the matrix to autonomously close its own cracks over time. In this study, specimens (50 mm in diameter and 25 mm in height) were exposed to submersion and a wet–dry cycle environment. The solution considered a nutrient-rich suspension with calcium lactate, urea, calcium nitrate, and Bacillus subtilis or Sporosarcina pasteurii in a biomineralization approach. The self-healing efficiency was assessed through optical microscopy combined with image processing, focusing on the analysis of the superficial crack closure area. S. and B. subtilis exhibited notable capabilities in effectively healing cracks, respectively, 8 mm2 and 5 mm2 at 35 days. Healing was particularly effective in samples placed in a submerged environment, especially with a 69 mM concentration of calcium lactate in bacterial suspensions containing B. subtilis, where 87.5% of a 4 mm2 crack was closed within 21 days. In contrast, free calcium ions in the solution, resulting from anhydrous cement hydration, proved ineffective for S. pasteurii biomineralization in urea-rich environments. However, the addition of an external calcium source (calcium nitrate) significantly enhanced crack closure, emphasizing the critical role of calcium availability in optimizing MICP for bio-agents in cement-based materials. These findings highlight the potential of MICP to advance sustainable self-healing concrete technologies.