Asset Details
Do you wish to reserve the book?
Pore–crack orientation effects on fracture behavior of brittle porous materials
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Pore–crack orientation effects on fracture behavior of brittle porous materials
Do you wish to request the book?
Pore–crack orientation effects on fracture behavior of brittle porous materials
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Pore–crack orientation effects on fracture behavior of brittle porous materials
2014
Overview
Mechanical behavior of two-dimensional microstructures containing circular pores were simulated under uniaxial and biaxial loading using the finite element method. Resulting stress distributions were combined with classical fracture mechanics to investigate fracture behavior of brittle porous materials assuming that randomly oriented cracks are present along pore surfaces. Multiple crack orientations were found to introduce a variability in Weibull modulus even for the same set of microstructures containing equal number and size of cracks. Also, the variability increases with increasing crack size to pore size ratio. Under uniaxial loading, angular distribution of fracture origin widens with increasing porosity.
Publisher
Springer Netherlands,Springer Nature B.V