Asset Details
Do you wish to reserve the book?
Piercing and surface-crack defects in combination extrusion of fasteners
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Piercing and surface-crack defects in combination extrusion of fasteners
Do you wish to request the book?
Piercing and surface-crack defects in combination extrusion of fasteners
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Conference Proceeding
Piercing and surface-crack defects in combination extrusion of fasteners
2017
Overview
Piercing or surface-crack defect occurs in combination-extruding the support pin. There has been so far insufficient knowledge in avoiding such forming defects in forming the similar products. In this paper, a combination-extrusion experiment, with various combinations of forward and backward extrusion ratios, was conducted to observe the occurrence of the defects. The result shows that the defects occur at low level of both forward extrusion ratio and backward extrusion ratio used in the combination-extrusion process. The low forming level causes the onset of insufficient plastic metal-flow, which is similar to that of inhomogeneous deformation in the unidirectional extrusion or drawing process. A forming limit diagram was constructed and can be used in the defect prediction for the future development of similar products.