Asset Details
Do you wish to reserve the book?
Interstitial-Free Bake Hardening Realized by Epsilon Martensite Reverse Transformation
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Interstitial-Free Bake Hardening Realized by Epsilon Martensite Reverse Transformation
Do you wish to request the book?
Interstitial-Free Bake Hardening Realized by Epsilon Martensite Reverse Transformation
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Interstitial-Free Bake Hardening Realized by Epsilon Martensite Reverse Transformation
2019
Overview
By investigating a metastable high-entropy alloy, we report a latent strengthening mechanism that is associated with the thermally-induced epsilon-martensite-to-austenite reverse transformation. We show this reversion-assisted hardening effect can be achieved in the same time-scale and temperature range as conventional bake-hardening treatment, but leads to both improved strength and cumulative ductility. Key mechanisms are discussed considering transformation kinetics, kinematics, strengthening and ductilization modules.