Asset Details
Do you wish to reserve the book?
تلوين بلورة \AL2O3\ باستخدام العناصر الانتقالية
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
تلوين بلورة \AL2O3\ باستخدام العناصر الانتقالية
Do you wish to request the book?
تلوين بلورة \AL2O3\ باستخدام العناصر الانتقالية
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
تلوين بلورة \AL2O3\ باستخدام العناصر الانتقالية
2022
Overview
شمل هذا البحث تلوين بلورة الالومينا باستخدام العناصر الانتقالية لإنتاج صبغات لونية، ولهذا الغرض تم تحديد أوكسيد الكوبلت (CoO) وبلورة الالومينا (Al2O3) وتم تحديد نوع الجسم الفخاري بطينة المحاويل. أما الحدود المكانية فكانت ضمن حدود محافظة بابل. وقد قام الباحث بتحضير ثلاث خلطات إذ تم تلوين البلورة (Al2O3) في الخلطة الأولى بـ (10%) كوبلت والثانية بـ (5%) والثالثة بـ (2.5%). بعدها وضعت هذه الخلطات في بوادق كل واحدة على حدة وأدخلت للفرن ليتم تفريتها بدرجة حرارة (1200م) وبشكل جاف بعدها أخرجت من الفرن ليتم طحن الناتج بواسطة (طاحونة كهربائية) وتطبيق الصبغة الناتجة على الأجسام الفخارية بعد أضافتها إلى الزجاج الجاهز وقد اعتمد أسلوب الحرق البطيء في ثلاث درجات حرارة (950م- 1000م- 1050م) في فرن كهربائي أظهرت النتائج إمكانية تلوين البلورة وإنتاج الصبغات اللونية، وإمكانية استخدام هذه الصبغات المنتجة في درجات الحرارة المختلفة وقد أظهرت النتائج أيضا ملاءمة هذه الصبغات للزجاج الجاهز وملائمتها للأجسام الخزفية.