Asset Details
Do you wish to reserve the book?
دراسة تأثر المعاملة الحرارية لمتراكب سيرميتي محضر بطريقة الرش الحراري باللهب
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
دراسة تأثر المعاملة الحرارية لمتراكب سيرميتي محضر بطريقة الرش الحراري باللهب
Do you wish to request the book?
دراسة تأثر المعاملة الحرارية لمتراكب سيرميتي محضر بطريقة الرش الحراري باللهب
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
دراسة تأثر المعاملة الحرارية لمتراكب سيرميتي محضر بطريقة الرش الحراري باللهب
2018
Overview
تم استخدام تقنية الرش الحراري باللهب في إنتاج مادة مركبة ذات أساس من الزركونيا نسبة %25 مقواه بدقائق سيراميكية من الألومينا نسبة %25 مع مادة رابطة من (Ni - Al) بنسبة %50 على قاعدة من سبيكة الفولاذ نوع (316L) بعد إن تم تهيئتها بطريقة التخشين بالعصف الحبيبي. أجريت عملية الرش باستخدام مسافة رش (16) سم. اختبارات الصلادة تم إجراءها على طبقة المادة المركبة المنتجة لدراسة تأثير تغير مسافة الرش على خواص الطبقة الناتجة. تم إجراء المعاملة الحرارية على العينات عند °C (1050.900) لمدة ساعة. أكدت نتائج الاختبارات بأن أفضل مسافة رش (16 cm) والمعاملة الحرارية C° (1050) حيث لهما تأثير كبير في تحسين خواص طبقات المادة المركبة المنتجة خاصة الصلادة.