Ultra High Early Strength Serf-compacting Mortar Based on Suifoaluminate Cement and Silica Fume

ZHU Yanehao MA Baoguo LI Xiangguo HU Di

2013

Overview

The influences of silica fume and aluminum sulfate on hydration process of sulfoaluminate cement were carried out by ring flow, setting time, hydration heat, XRD and DTG analyses. In addition, mortar mixtures with different functional additives have been studied through compressive strength, flexural strength, volume stability at early age and porosity characterization tests. The results show that the addition of silica fume and aluminum sulfate reduces the fluidity and shortens the setting time of sulfoaluminate cement paste, promoting hydration process and increasing hydration products at early age. In the case of appropriate proportion of mortar, the inclusion of hydroxy propyl methyl cellulose, dispersible polypropylene fiber arid organic silicon kind of defoamer can control segregation and bleeding, improve mechanical strength and volume stability at early age, and modify the pore distribution of sulfoaluminate cement mortar, respectively. The sulfoaluminate cement mortar can carry out gravitational grouting in the absence of outside force, the compressive strength of 2 hours and 24 hours have reached 26 and 58 MPa respectively, and have good micro- expansion and tiny.pore distribution characterization.

• Subject: 体积稳定性 / 功能性添加剂 / 密实 / 水化过程 / 混合砂浆 / 硅粉 / 硫铝酸盐水泥 / 超早强