Asset Details
Do you wish to reserve the book?
Effect of graphite powder as a forming filler on the mechanical properties of SiCp/AI composites by pressure infiltration
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Effect of graphite powder as a forming filler on the mechanical properties of SiCp/AI composites by pressure infiltration
Do you wish to request the book?
Effect of graphite powder as a forming filler on the mechanical properties of SiCp/AI composites by pressure infiltration
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Effect of graphite powder as a forming filler on the mechanical properties of SiCp/AI composites by pressure infiltration
2016
Overview
（38vo1% SiCp ＋ 2vo1% A1203f）/2024 A1 composites were fabricated by pressure infiltration. Graphite powder was introduced as a forming filler in preform preparation, and the effects of the powder size on the microstructures and mechanical properties of the final com- posites were investigated. The results showed that the composite with 15 μm graphite powder as a forming filler had the maximum tensile strength of 506 MPa, maximum yield strength of 489 MPa, and maximum elongation of 1.2%, which decreased to 490 MPa, 430 MPa, and 0.4%, respectively, on increasing the graphite powder size from 15 to 60 μm. The composite with 60 μm graphite powder showed the highest elastic modulus, and the value decreased from 129 to 113 GPa on decreasing the graphite powder size from 60 to 15 μm. The differences between these properties are related to the different microstructures of the corresponding composites, which determine their failure modes.