Asset Details
Do you wish to reserve the book?
Effect of Curing Temperature on the Properties of a MgO-SiOsub.2-Hsub.2O System Prepared Using Dead-Burned MgO
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Effect of Curing Temperature on the Properties of a MgO-SiOsub.2-Hsub.2O System Prepared Using Dead-Burned MgO
Do you wish to request the book?
Effect of Curing Temperature on the Properties of a MgO-SiOsub.2-Hsub.2O System Prepared Using Dead-Burned MgO
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Effect of Curing Temperature on the Properties of a MgO-SiOsub.2-Hsub.2O System Prepared Using Dead-Burned MgO
2022
Overview
The hydration of M-S-H prepared using silica fume (SF) and dead-burned MgO cured at 20 °C, 50 °C, and 80 °C was investigated, and the properties and performance of this M-S-H were measured. The formation of M-S-H was characterized using XRD, FTIR, TGA, and [sup.29]Si MAS-NMR. Results show that the compressive strength of paste prepared using MgO calcined at 1450 °C for 2 h reached 25 MPa after 28 d. The shrinkage of mortar made with low reactivity MgO was lower than that made with high reactivity MgO. The pH value of MgO/SF paste mixed with dead-burned MgO did not exceed 10.4 at room temperature. The shrinkage of M-S-H prepared using dead-burned MgO was less than that prepared using more active MgO, and its strength did not decrease over time. No (or only a small amount of) Mg(OH)[sub.2] was formed, which is why the strength of M-S-H prepared with dead-burned MgO continually increased, without decreasing. The promotion of curing temperature favor process of MgO hydration and is beneficial for degree of silica polymerization. The sample cured in 50 °C water showed the highest relative degree of reaction.