Asset Details
Do you wish to reserve the book?
Nano-Ridge Engineering of GaSb for the Integration of InAs/GaSb Heterostructures on 300 mm Si
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Nano-Ridge Engineering of GaSb for the Integration of InAs/GaSb Heterostructures on 300 mm Si
Do you wish to request the book?
Nano-Ridge Engineering of GaSb for the Integration of InAs/GaSb Heterostructures on 300 mm Si
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Nano-Ridge Engineering of GaSb for the Integration of InAs/GaSb Heterostructures on 300 mm Si
2020
Overview
Nano-ridge engineering (NRE) is a novel heteroepitaxial approach for the monolithic integration of lattice-mismatched III-V devices on Si substrates. It has been successfully applied to GaAs for the realization of nano-ridge (NR) laser diodes and heterojunction bipolar transistors on 300 mm Si wafers. In this report we extend NRE to GaSb for the integration of narrow bandgap heterostructures on Si. GaSb is deposited by selective area growth in narrow oxide trenches fabricated on 300 mm Si substrates to reduce the defect density by aspect ratio trapping. The GaSb growth is continued and the NR shape on top of the oxide pattern is manipulated via NRE to achieve a broad (001) NR surface. The impact of different seed layers (GaAs and InAs) on the threading dislocation and planar defect densities in the GaSb NRs is investigated as a function of trench width by using transmission electron microscopy (TEM) as well as electron channeling contrast imaging (ECCI), which provides significantly better defect statistics in comparison to TEM only. An InAs/GaSb multi-layer heterostructure is added on top of an optimized NR structure. The high crystal quality and low defect density emphasize the potential of this monolithic integration approach for infrared optoelectronic devices on 300 mm Si substrates.