Dissertation

Abnormal grain growth in iron-silicon

Bennett, Tricia A

2006

Overview

Abnormal grain growth (AGG) was studied in an Fe-1%Si alloy using automated Electron Backscattered Diffraction (EBSD) to determine the driving force for this phenomenon. Experiments were performed with the knowledge that there are several possible driving forces and, the intent to determine the true driving force by elimination of the other potential candidates. These potential candidates include surface energy anisotropy, anisotropic grain boundary properties and the stored energy of deformation. In this work, surface energy and grain boundary anisotropies as well as the stored energy of deformation were investigated as the possible driving forces for AGG. Accordingly, industrially processed samples that were temper rolled to 1.5% and 8% were annealed in air for various times followed by quenching in water. The results obtained were compared to those from heat treatments performed in wet 15%H2-85%N2 at a US Steel facility. In addition, for a more complete study of the effect of surface energy anisotropies on AGG, the 1.5% temper-rolled material was heat-treated in other atmospheres such as 5%H2-95%Ar, 98%H2-2%He, 98%H2-2%H 2S, and 98%H2-2%N2 for 1 hour followed by quenching in water. The character of the grain boundaries in the materials was also examined for each set of experiments conducted, while the influence of stored energy was evaluated by examining intragranular orientation gradients. AGG occurred regardless of annealing atmosphere though the most rapid progression was observed in samples annealed in air. In general, grains of varying orientations grew abnormally. One consistently observed trend in all the detailed studies was that the matrix grains remained essentially static and either did not grow or only grew very slowly. On the other hand, the abnormally large grains (ALG), on average, were approximately 10 times the size of the matrix. Analysis of the grain boundary character of the interfaces between abnormal grains and the matrix showed no significant variation from the overall population of boundaries. This suggested that grain boundary character was not a factor in controlling AGG. When the effect of stored energy differences was considered, it was observed that grains that experienced AGG had low orientation gradients. Based on these results and cross comparison of all classes of experiments performed, it was determined that stored energy differences were the main driving force for AGG in this Fe-1%Si alloy.

• Publisher: ProQuest Dissertations & Theses
• Subject: Materials science
• ISBN: 9798607372347