Phonons and Hybrid Modes in the High and Low Temperature Far Infrared Dynamics of Hexagonal TmMnO3

Alonso, José Antonio, Domingos De Sousa Meneses, Echegut, Patrick, Leire del Campo, María Jesús Martínez-Lope, Massa, Néstor E

2014

Overview

We report on TmMnO3 far infrared emissivity and reflectivity spectra from 1910 K to 4 K. At the highest temperature the number of infrared bands is lower than that predicted for centrosymmetric P63/mmc (D6h4) (Z=2) space group due high temperature anharmonicity and possible defect induced bitetrahedra misalignments. On cooling, at ~1600 K TmMnO3 goes from non-polar to an antiferroelectric-ferroelectric polar phase reaching the ferroelectric onset at the ~700 K. The 300 K reflectivity is fitted using 19 oscillators and this number of phonons is maintained down to 4 K. A weak phonon anomaly in the band profile at 217 cm-1 (4 K) suggests subtle Rare Earth magnetoelectric couplings at ~TN and below. A low energy collective excitation is identified as a THz instability associated with room temperature eg electrons in a d-orbital fluctuating environment. It condenses into two modes that emerge pinned to the E-type antiferromagmetic order hardening simultaneously down to 4 K. They obey power laws with TN as the critical temperature and match known zone center magnons. The one peaking at 26 cm-1, with critical exponent \\b{eta}=0.42 as for antiferromagnetic order in a hexagonal lattice, is dependent on the Rare Earth. The band at ~50 cm-1, with \\b{eta}=0.25, splits at ~TN into two peaks. The weaker band of the two is assimilated to the upper branch of gap opening in the transverse acoustical (TA) phonon branch crossing the magnetic dispersion found in YMnO3. (Petit et al, 2007 PRL 99, 266604). The stronger second at ~36 cm-1 corresponds to the lower branch of the TA gap. We assign both excitations as zone center magnetoelectric hybrid quasiparticles concluding that in NdMnO3 perovskite the equivalent picture corresponds to an instability which may be driven by an external field to transform NdMnO3 into a multiferroic compound by perturbation enhancing the TA phonon-magnetic correlation.

• Publisher: Cornell University Library, arXiv.org
• Subject: Anharmonicity / Antiferroelectricity / Antiferromagnetism / Couplings / Critical temperature / Excitation / Far infrared radiation / Ferroelectric materials / Hexagonal lattice / High temperature / Hybrid modes / Infrared spectra / Lattice vibration / Magnetic dispersion / Magnons / Oscillators / Perovskites / Perturbation / Phonons / Reflectance / Temperature / Variations