Asset Details
Do you wish to reserve the book?
Ductile Cast Iron Microstructure Adjustment by Means of Heat Treatment
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Ductile Cast Iron Microstructure Adjustment by Means of Heat Treatment
Do you wish to request the book?
Ductile Cast Iron Microstructure Adjustment by Means of Heat Treatment
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Ductile Cast Iron Microstructure Adjustment by Means of Heat Treatment
2020
Overview
The study presented in this paper concerned the possibility to apply a heat treatment process to ductile cast-iron thin-walled castings in order to remove excessive quantities of pearlite and eutectic cementite precipitates and thus meet the customer’s requirements. After determining the rates of heating a casting up to and cooling down from 900°C feasible in the used production heat treatment furnace (vh = 300°C/h and vc = 200°C/h, respectively), dilatometric tests were carried out to evaluate temperatures Tgr, TAc1start, TAc1end, TAr1start, and TAr1end. The newly acquired knowledge was the base on which conditions for a single-step ferritizing heat treatment securing disintegration of pearlite were developed as well as those of a two-step ferritization process guaranteeing complete disintegration of cementite and arriving at the required ferrite and pearlite content. A purely ferritic matrix and hardness of 119 HB was secured by the treatment scheme: 920°C for 2 hours / vc = 60°C/h / 720°C for 4 hours. A matrix containing 20–45% of pearlite and hardness of 180–182 HB was obtained by applying: 920°C for 2 hours or 4 hours / vc = 200°C/h to 650°C / ambient air.