Asset Details
Do you wish to reserve the book?
Influence of Cathodic Polarization on Plasma Electrolytic Oxidation of Magnesium and AZ31 and AZ91 Magnesium Alloys
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Influence of Cathodic Polarization on Plasma Electrolytic Oxidation of Magnesium and AZ31 and AZ91 Magnesium Alloys
Do you wish to request the book?
Influence of Cathodic Polarization on Plasma Electrolytic Oxidation of Magnesium and AZ31 and AZ91 Magnesium Alloys
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Influence of Cathodic Polarization on Plasma Electrolytic Oxidation of Magnesium and AZ31 and AZ91 Magnesium Alloys
2023
Overview
In this study, the influence of cathodic polarization on the plasma electrolytic oxidation (PEO) behaviors of pure magnesium and AZ31 and AZ91 magnesium alloys with varied Al alloying contents was systematically examined in a dilute alkaline silicate electrolyte by adjusting the cathodic-to-anodic current density ratio (R = jc/ja) from 0 to 3.2. The results show that moderate cathodic polarization (R = 0.6) led to the thickest coatings on the Mg and Mg alloys, and the coatings grew in an outward-and-inward mode compared with the inward growth at R = 0. Excessive cathodic polarization (high R ratios) differently influenced the PEO behaviors of the magnesium alloys. For the pure magnesium and AZ31 alloy, the coatings blistered or peeled off when the R ≥ 0.9. However, the tolerance to cathodic polarization was significantly improved for the AZ91 Mg alloy. The coatings were undamaged even with the highest R ratio of 3.2, and their compactness was further improved as the R ratio increased to 0.9 and 1.2. An increase in cathodic polarization led to a reduction in the anodic potential and spark softening but did not result in an improvement in the coating quality. Optical emission spectroscopy identified two spectral lines at 559.79 and 570.11 nm, which are assigned to the Mg species but not found in databases or the literature. The corrosion and wear resistance of the PEO coatings were also investigated. The coating formed on the AZ91 magnesium alloy at R = 1.2 displayed the narrowest wear track due to its high compactness.