Asset Details
Do you wish to reserve the book?
Study on synthesis and application of copolymer poly(N,N-Diethylacrylamide-co-Acrylamide)
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Study on synthesis and application of copolymer poly(N,N-Diethylacrylamide-co-Acrylamide)
Do you wish to request the book?
Study on synthesis and application of copolymer poly(N,N-Diethylacrylamide-co-Acrylamide)
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Study on synthesis and application of copolymer poly(N,N-Diethylacrylamide-co-Acrylamide)
2025
Overview
Temperature-sensitive copolymer is an important functional material, and its directional application in different fields is a hotspot in recent years. This work introduced temperature-sensitive polymers into membrane materials for separation and enrichment of metal ions, and the process was designed as follows: Firstly, the temperature-sensitive copolymers of P (N, N-diethylacrylamide-co-acrylamide) (P(DEA-co-AM)) was successfully synthesized with different monomer feed ratios by radical polymerization at 70 °C. Secondly, series characterization methods were adopted to study the structure of samples, and following results were achieved. After integrating the characteristic peak areas of the
1
H NMR, reactive ratios of DEA and AM was obtained by Fineman-Ross method(F-R) and Kelen-Tudos method(K-T), respectively, and result also evidenced that as the feed molar ratio of DEA to AM was 8: 2, the average segment length ratio between AM and DEA in P (DEA-co-AM) were 1.073: 8.072, respectively. FT-IR and DSC characterization results shown that the synthesized polymer was copolymer and random copolymer, respectively, UV–visible spectrophotometer test result showed the copolymer exhibited a good thermosensitive. Finally, a smart imprinted membrane was prepared by this copolymer with PVDF and was used for selectively adsorbing ruthenium (III) from the complex environmental, and experiments results documented that the imprinted membrane displayed a good adsorption capacity, which provided a great development potential in separation and enrichment of ruthenium (III) fields.