Effect of Pre-Strain on Microstructure and Tensile Properties of Ti-6Al-4V at Elevated Temperature

Wang, Ning, Wu, Taowen, Shi, Wenxiang, Chen, Minghe, Zuo, Dunwen, Xie, Lansheng

2021

Overview

Research on pre-deformation influences on material properties in multistep hot forming is of important scientific interest. In this paper, hot tensile tests at 850 °C and a strain rate of 0.001 s−1 were performed to study the microstructural evolution and mechanical properties of Ti-6Al-4V with pre-strains at 0.05, 0.1 and 0.15. The tensile test results showed that the specimen with 0.05 pre-strain exhibited higher flow stress and larger elongation. Additionally, increasing the pre-strain resulted in a decrease in ultimate tensile strength (UTS) and elongation (EL). The EBSD results showed that the main deformation mechanism of Ti-6Al-4V was high-angle grain boundary sliding. Pre-strain promoted dynamic recrystallization (DRX) by increasing the deformation substructure. The refinement of grains and the eradication of dislocations enhanced the deformability, resulting in an increase in flow stress.

• Publisher: MDPI AG
• Subject: Deformation / Deformation mechanisms / Dislocations / Dynamic recrystallization / Elongation / Formability / Grain boundaries / Grain boundary sliding / Grain size / High temperature / Hot forming / Material properties / Mechanical properties / Microstructure / microstructure evolution / Phase transitions / pre-deformation / Predeformation / Strain rate / Temperature / Tensile properties / Tensile strength / Tensile tests / Ti-6Al-4V titanium alloy / Titanium alloys / Titanium base alloys / Ultimate tensile strength / Yield strength