Asset Details
Do you wish to reserve the book?
Increasing the Hydration Activity of Tricalcium Silicate by Adding Microdispersed Ettringite as a Nucleating Agent
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Increasing the Hydration Activity of Tricalcium Silicate by Adding Microdispersed Ettringite as a Nucleating Agent
Do you wish to request the book?
Increasing the Hydration Activity of Tricalcium Silicate by Adding Microdispersed Ettringite as a Nucleating Agent
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Increasing the Hydration Activity of Tricalcium Silicate by Adding Microdispersed Ettringite as a Nucleating Agent
2023
Overview
Tricalcium silicate (C3S) as a binder material has a decisive influence on the processes of hardening and strength gain of cements and concretes. One of the promising directions is the introduction of dispersed additives into cement mixtures, which allow micro-level control of the composition of hydration products and change the dynamics of the structure formation of cement stone. In this paper, the effect of a microdisperse ettringite additive on the kinetics of the hydration and hardening process of tricalcium silicate was studied. It was shown that ettringite crystals selectively adsorb Ca2+ and OH− ions from a saturated solution of calcium hydroxide, which contributes to the formation of hydrosilicate nuclei on their surface during cement hydration. Hydration of C3S in the presence of ettringite proceeds more intensively; the addition of ettringite contributes to an increase in the content of calcium hydrosilicates in hydration products at the initial stage of the process. Addition of 10 wt.% ettringite to C3S reduces the induction period of the beginning of the main phase of heat release by around two times and increases the amount of heat released on the 1st day of hydration by 15% compared to the control sample. According to electron microscopy data, it was found that during the first hours of hydration of modified C3S, a significant number of nuclei of fibrous particles of calcium hydrosilicates with sizes of 0.2–2 microns were formed on the surface of ettringite crystals. According to the results of kinetic modeling of the setting process of cement pastes using the Avrami–Erofeyev model, it was shown that in the presence of the addition of microcrystals of ettringite, the setting rate is characterized by a slowdown in nucleation, whereas for a sample without an additive, this process proceeds with an acceleration of the formation of solid-phase nuclei. Based on the comparison of kinetic results and mechanical measurements, it is concluded that needle crystals of ettringite during C3S hydration and cement stone hardening are preformed centers for the growth of hydrosilicate nuclei, and they also act as a reinforcing filler, increasing the bending strength of modified samples. The results of the work can be used in practice in the development of methods for controlling the processes of hydration and hardening of cements, as well as for controllable structure formation of cement stone which is important in particular for 3D printing of building products and constructions.