Asset Details
Do you wish to reserve the book?
Microstructure and Hot Oxidation Resistance of SiMo Ductile Cast Irons Containing Si-Mo-Al
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Microstructure and Hot Oxidation Resistance of SiMo Ductile Cast Irons Containing Si-Mo-Al
Do you wish to request the book?
Microstructure and Hot Oxidation Resistance of SiMo Ductile Cast Irons Containing Si-Mo-Al
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Microstructure and Hot Oxidation Resistance of SiMo Ductile Cast Irons Containing Si-Mo-Al
2017
Overview
SiMo ductile cast irons are used as high-temperature materials in automotive components, because they are microstructurally stable at high operating temperatures. The effect of different amounts of Si and Mo as well as the addition of 3 wt pct Al on the microstructure, high-temperature oxidation, and mechanical properties of SiMo ductile cast iron was studied. Dilatometric measurements of SiMo ductile iron exhibited obvious differences in the transformation temperature
A
1
due to presence of Al and the increase of Si. The microstructure of the SiMo alloys without Al addition showed outstanding nodularity and uniform nodule distribution. However, by adding 3 wt pct Al to low Si-SiMo ductile iron, some compacted graphite was observed. The results of oxidation experiments indicated that high Si-SiMo ductile iron containing 4 and 4.9 wt pct Si had superior resistance to lower Si-SiMo and SiMo ductile iron containing 3 wt pct Al. The results showed also that with increasing Si up to 4.9 wt pct or by replacing a part of Si with 3 wt pct Al, tensile strength increased while elongation and impact toughness decreased.