Effects of Rare Earth La–Ce Alloying Treatment on Modification of Inclusions and Magnetic Properties of W350 Non-Oriented Silicon Steel

Zhong, Wei, Zhang, Yanling, Wang, Haijun, Niu, Yuhao, Qiao, Jialong, Qiu, Shengtao, Ling, Haitao

2023

Overview

In order to study the effects of rare earth La–Ce alloying treatment on the characteristics of inclusions in non-oriented silicon steels, industrial experiments were conducted studying the composition, morphology, size and quantity of inclusions in W350 non-oriented silicon steel during the RH (Ruhrstahl-Hereaeus) refining process and tundish process, after rare earth treatment. The products were analyzed by means of ICP-MS (inductively coupled plasma mass spectrometry), SEM/EDS (scanning electron microscope-energy dispersive spectrometry), and ASPEX (automated SEM/EDS inclusion analysis). The research results showed that the types of inclusions in experimental steel changed significantly after rare earth treatment. The types of inclusions after RE (rare earth) treatment are typically rare earth composite inclusions that are mainly composed of (La, Ce)Al2O3, and conventional inclusions. The addition of rare earth promotes the agglomeration of inclusions; the morphologies of the inclusions are mostly blocky, and some are distributed in long strips. After rare earth treatment during the RH refining process, the number of inclusions with sizes of 1.0~3.5 μm in the experimental steel is increased, and the average size of the inclusions is 2.66 μm. In addition, the number of inclusions larger than 4 μm in the specimens increases due to the collision and growth of inclusions caused by the RH circulation. After rare earth treatment during the tundish process, the number of micro inclusions with sizes of 1.0~2.5 μm in the specimen steels decreases, while the number of inclusions larger than 5 μm increases. The size distribution of micro inclusions in hot-rolled sheets after rare earth treatment was studied using TEM (transmission electron microscopy). In the specimens without rare earth, the content of micro inclusions (≤1 μm) is 51,458.2/mm2 and the average size is 0.388 μm. In the specimens with rare earth added, the content of micro inclusions (≤1 μm) is 24,230.2/mm2 and the average size is 0.427 μm. Compared to sheet produced by the original process, the iron loss of the 0.35 mm finished experimental sheet is reduced by 0.068 W/kg, and the magnetic induction is increased by 0.007 T. The iron loss of the 0.50 mm finished experimental sheet is reduced by 0.008 W/kg, and the magnetic induction is increased by 0.004 T. After rare earth treatment, the average size of micro inclusions increases and the magnetic properties are obviously improved.

• Publisher: MDPI AG
• Subject: Alloying / Aluminum oxide / Cerium / Core loss / Efficiency / Hot rolling / Inclusions / Inductively coupled plasma mass spectrometry / Lanthanum / Magnetic induction / Magnetic properties / magnetic property / Magnetization / Mass spectrometry / modification / Morphology / non-oriented silicon steel / Rare earth elements / rare earth La–Ce / Scanning electron microscopy / Silicon / Silicon steel / Silicon steels / Size distribution / Specialty metals industry / Steel products / Trace elements / Tundishes