Asset Details
Do you wish to reserve the book?
Inorganic Acid Resistance Performances of Magnesium Phosphate Cement: A Two-Year Observation
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Inorganic Acid Resistance Performances of Magnesium Phosphate Cement: A Two-Year Observation
Do you wish to request the book?
Inorganic Acid Resistance Performances of Magnesium Phosphate Cement: A Two-Year Observation
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Inorganic Acid Resistance Performances of Magnesium Phosphate Cement: A Two-Year Observation
2024
Overview
Magnesium phosphate cement (MPC), a cementitious material that hardens through an acid–base reaction, is theoretically expected to exhibit strong acid resistance. However, studies on the durability of MPC in acidic environments remain limited. This study aims to systematically evaluate the acid resistance of MPC in common inorganic acid solutions across various pH levels. By measuring changes in compressive strength, mass loss, apparent changes, pH changes, and the microstructure evolution of MPC under acidic conditions, the mechanisms and influencing factors of its acid resistance are revealed. The results indicate that at pH levels of 1.0 and 2.0, MPC’s resistance to H2SO4 and HCl erosion is markedly superior compared to its performance against H3PO4, as evidenced by compressive strength retention, mass loss, and visible erosion. At pH levels above 2.0, MPC demonstrates robust resistance to all tested corrosive media, with compressive strength retention ranging from 68.9% to 86.9%, irrespective of the acid source. Although new corrosion products form in these acidic environments, the adverse effects of NH4/P loss from struvite, along with the redissolution of corrosion products due to their higher solubility, increase porosity and subsequently reduce the mechanical strength. Nevertheless, considering that strength retention is significantly higher than that of other cement-based materials reported in the literature, MPC still exhibits good acid resistance and is suitable for environments requiring enhanced resistance to acid corrosion.