Asset Details
Do you wish to reserve the book?
Effect of Changing Climatic Conditions on Properties of Wood Textile Composites
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Effect of Changing Climatic Conditions on Properties of Wood Textile Composites
Do you wish to request the book?
Effect of Changing Climatic Conditions on Properties of Wood Textile Composites
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Effect of Changing Climatic Conditions on Properties of Wood Textile Composites
2025
Overview
Wood–textile composites (WTCs), consisting of polypropylene and woven willow wood, have potential for both interior and exterior applications. However, their basic materials are not inherently resistant to outdoor weathering. This study examines the impact of various climatic conditions on the material behavior of WTCs. The composite and its components were aged under different scenarios, including kiln-drying, frost, standard and tropical climate, and artificial weathering and water storage, and analyzed for dimensional stability, chemical changes (FTIR), mechanical damage (µ-CT), and mechanical performance. While kiln-drying, frost, and tropical climates had only minor effects, water storage caused swelling-related damage, resulting in a 45% decrease in Young’s modulus but increased elongation at break (+88%) and impact strength (+75%). Artificial weathering led to significant degradation: tensile strength declined by 28%, Young’s modulus by 49%, and impact strength by 26%. In the medium term, this degradation compromises the integrity of the composite. The results highlight the need for effective stabilization measures—such as polymer modification or structural protection—to ensure the long-term durability of WTCs in outdoor use.