Asset Details
Do you wish to reserve the book?
Hot deformation behavior of GH4945 superalloy using constitutive equation and processing map
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Hot deformation behavior of GH4945 superalloy using constitutive equation and processing map
Do you wish to request the book?
Hot deformation behavior of GH4945 superalloy using constitutive equation and processing map
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Hot deformation behavior of GH4945 superalloy using constitutive equation and processing map
2017
Overview
The hot deformation behavior of GH4945 superalloy was investigated by isothermal compression test in the temperature range of 1000--1200 ℃with strain rates of 0.001 10.000 s 1 toa total strain of 0.7. Dynamic recrystallization is the primary softening mechanism for GH4945 superalloy during hot deformation. The constitutive equation is established, and the calculated apparent activation energy is 458. 446 kJ/moh The processing maps at true strains of 0.2, 0.4 and 0.6 are generally similar, dem- onstrating that strain has little influence on processing map. The power dissipation efficiency and in- stability factors are remarkably influenced by deformation temperature and strain rate. The optimal hot working conditions are determined in temperature range of 1082 -1131 ℃ with strain rates of 0.004--0.018 s-1. Another domain of1134--1150 ℃ and 0. 018 0.213s ^- can also be selected as the optimal hot working conditions. The initial grains are replaced by dynamically reerystallized ones in optimal domains. The unsafe domains locate in the zone with strain rates above 0, 274 s^- 1, mainly characterized by uneven microstructure. Hot working is not recommended in the unsafe domains.