Asset Details
Do you wish to reserve the book?
Effect of Thermal Load Caused by Tread Braking on Crack Propagation in Railway Wheels on Long Downhill Ramps
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Effect of Thermal Load Caused by Tread Braking on Crack Propagation in Railway Wheels on Long Downhill Ramps
Do you wish to request the book?
Effect of Thermal Load Caused by Tread Braking on Crack Propagation in Railway Wheels on Long Downhill Ramps
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Effect of Thermal Load Caused by Tread Braking on Crack Propagation in Railway Wheels on Long Downhill Ramps
2024
Overview
To investigate the propagation behavior of thermal cracks on the wheel tread under the conditions of long downhill ramps, a three-dimensional finite element model of a 1/16 wheel, including an initial thermal crack, was developed using the finite element software ANSYS 17.0. The loading scenarios considered include mechanical wheel–rail loads, both with and without the superposition of thermal wheel–brake shoe friction loads. The virtual crack closure method (VCCM) is employed to analyze the variations in stress intensity factors (SIFs) for Modes I, II, and III (KI, KII, and KIII) at the 0°, mid, and 90° positions along the crack tip. The simulation results show that temperature is a critical factor for the propagation of thermal cracks. Among the SIFs, KII (Mode II) is larger than KI (Mode I) and KIII (Mode III). Specifically, the thermal load on the wheel tread during braking contributes up to 23.83% to KII when the wheel tread reaches the martensitic phase transition temperature due to brake failure. These results are consistent with the observed radial propagation of thermal cracks in wheel treads under operational conditions.