Asset Details
Do you wish to reserve the book?
Effects of Overload on Thermal Decomposition Kinetics of Cross-Linked Polyethylene Copper Wires
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Effects of Overload on Thermal Decomposition Kinetics of Cross-Linked Polyethylene Copper Wires
Do you wish to request the book?
Effects of Overload on Thermal Decomposition Kinetics of Cross-Linked Polyethylene Copper Wires
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Effects of Overload on Thermal Decomposition Kinetics of Cross-Linked Polyethylene Copper Wires
2023
Overview
During an overload fault in an energized wire, the hot metal core modifies the structure of the insulation material. Therefore, understanding the thermal decomposition kinetics of the insulation materials of the overloaded wire is essential for fire prevention and control. This study investigates the thermal decomposition process of new and overloaded cross-linked polyethylene (XLPE) copper wires using thermogravimetry–Fourier-transform infrared spectroscopy and cone calorimetry. The thermal decomposition onset temperature and activation energy of the overloaded XLPE insulation materials were reduced by approximately 15 K and 20 kJ mol−1, respectively, and its reaction mechanism function changed from D-ZLT3 to A2 (0 < α < 0.5). The FTIR shows that the major spectral components produced during the pyrolysis of the XLPE insulation material are C-H stretching, H2O, CO2, C-H scissor vibrations, and C=O and C=C stretching. Additionally, the four functional groups in the PE chains produced the spectral components in the following decreasing order of wavenumber: C–H stretching > CO2 > C–H scissor vibration > C=O and C=C stretching.