Asset Details
Do you wish to reserve the book?
Degradation mechanisms of perovskite solar cells under vacuum and one atmosphere of nitrogen
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Degradation mechanisms of perovskite solar cells under vacuum and one atmosphere of nitrogen
Do you wish to request the book?
Degradation mechanisms of perovskite solar cells under vacuum and one atmosphere of nitrogen
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Degradation mechanisms of perovskite solar cells under vacuum and one atmosphere of nitrogen
2021
Overview
Extensive studies have focused on improving the operational stability of perovskite solar cells, but few have surveyed the fundamental degradation mechanisms. One aspect overlooked in earlier works is the effect of the atmosphere on device performance during operation. Here we investigate the degradation mechanisms of perovskite solar cells operated under vacuum and under a nitrogen atmosphere using synchrotron radiation-based operando grazing-incidence X-ray scattering methods. Unlike the observations described in previous reports, we find that light-induced phase segregation, lattice shrinkage and morphology deformation occur under vacuum. Under nitrogen, only lattice shrinkage appears during the operation of solar cells, resulting in better device stability. The different behaviour under nitrogen is attributed to a larger energy barrier for lattice distortion and phase segregation. Finally, we find that the migration of excessive PbI
2
to the interface between the perovskite and the hole transport layer degrades the performance of devices under vacuum or under nitrogen.
Understanding degradation mechanisms in perovskite solar cells is key to their development. Now, Guo et al. show a greater degradation of the perovskite structure and morphology for devices operated under vacuum than under nitrogen.