Asset Details
Do you wish to reserve the book?
Effects of Calcination on the Crystallography and Nonbiogenic Aragonite Formation of Ark Clam Shell under Ambient Condition
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Effects of Calcination on the Crystallography and Nonbiogenic Aragonite Formation of Ark Clam Shell under Ambient Condition
Do you wish to request the book?
Effects of Calcination on the Crystallography and Nonbiogenic Aragonite Formation of Ark Clam Shell under Ambient Condition
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Effects of Calcination on the Crystallography and Nonbiogenic Aragonite Formation of Ark Clam Shell under Ambient Condition
2016
Overview
This paper presents a study of crystallographic evolution of disposed ark clam shell (ACS) after calcination at 400–1400°C which was kept at room temperature under ambient condition in Malaysia during nine months. A better understanding of hydration and recarbonation of ACS powder (≤63 μm) after calcination was discovered by PXRD and FTIR. The research focuses on the crystallographic transformation, biogenic calcite decomposition, and unusual atmospheric aragonite formation in ACS after calcination and atmospheric air exposure. Ex situ PXRD showed calcite present in ACS at ≤900°C. ACS transformed to pyrogenic fcc CaO at ≥800°C after three months. Long term atmospheric air exposure of decarbonized ACS caused nucleation of nonbiogenic aragonite, vaterite, calcite, and portlandite. However, in situ PXRD analysis of ACS at instantaneous temperature without cooling process does not indicate the presence of aragonite, vaterite, and portlandite crystals. FTIR spectra revealed CaO–CO2 bond in ACS dissociated with temperature (600–900°C) to form CaO and CO2. Ca–OH bond was also traced in FTIR spectra of ≥700°C. It resulted by hydroadsorption of CaO with H2O in atmospheric air.