Asset Details
Do you wish to reserve the book?
Activation and Disproportionation of Zr2Fe Alloy as Hydrogen Storage Material
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Activation and Disproportionation of Zr2Fe Alloy as Hydrogen Storage Material
Do you wish to request the book?
Activation and Disproportionation of Zr2Fe Alloy as Hydrogen Storage Material
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Activation and Disproportionation of Zr2Fe Alloy as Hydrogen Storage Material
2019
Overview
As a hydrogen storage material, Zr2Fe alloy has many advantages such as fast hydrogen absorption speed, high tritium recovery efficiency, strong anti-pulverization ability, and difficulty self-igniting in air. Zr2Fe alloy has lower hydrogen absorption pressure at room temperature than LaNi5 alloy. Compared with the ZrVFe alloy, the hydrogen release temperature of Zr2Fe is lower so that the material can recover hydrogen isotopes at lower hydrogen concentration efficiently. Unfortunately, the main problem of Zr2Fe alloy in application is that a disproportionation reaction is easy to occur after hydrogen absorption at high temperature. At present, there is little research on the generation and influencing factors of a disproportionation reaction in Zr2Fe alloy. In this paper, the effects of temperature and hydrogen pressure on the disproportionation of Zr2Fe alloy were studied systematically. The specific activation conditions and experimental parameters for reducing alloy disproportionation are given, which provide a reference for the specific application of Zr2Fe alloy.