Asset Details
Do you wish to reserve the book?
Inhibiting weld cracking in high-strength aluminium alloys
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Inhibiting weld cracking in high-strength aluminium alloys
Do you wish to request the book?
Inhibiting weld cracking in high-strength aluminium alloys
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Inhibiting weld cracking in high-strength aluminium alloys
2022
Overview
Cracking from a fine equiaxed zone (FQZ), often just tens of microns across, plagues the welding of 7000 series aluminum alloys. Using a multiscale correlative methodology, from the millimeter scale to the nanoscale, we shed light on the strengthening mechanisms and the resulting intergranular failure at the FQZ. We show that intergranular AlCuMg phases give rise to cracking by micro-void nucleation and subsequent link-up due to the plastic incompatibility between the hard phases and soft (low precipitate density) grain interiors in the FQZ. To mitigate this, we propose a hybrid welding strategy exploiting laser beam oscillation and a pulsed magnetic field. This achieves a wavy and interrupted FQZ along with a higher precipitate density, thereby considerably increasing tensile strength over conventionally hybrid welded butt joints, and even friction stir welds.
Fusion welding of 7000 series aluminum alloy is plagued by cracking from a fine equiaxed zone (FQZ). Here, the authors quantify key softening mechanisms, show the damage accumulation sequence, and propose a hybrid laser/arc welding strategy to mitigate the FQZ and increase weld strength and toughness.