Asset Details
Do you wish to reserve the book?
Effects of bioactive glass incorporation into glass ionomer cement on demineralized dentin
Hey, we have placed the reservation for you!
By the way, why not check out events that you can attend while you pick your title.
Oops! Something went wrong.
Looks like we were not able to place the reservation. Kindly try again later.
Are you sure you want to remove the book from the shelf?
Effects of bioactive glass incorporation into glass ionomer cement on demineralized dentin
Do you wish to request the book?
Effects of bioactive glass incorporation into glass ionomer cement on demineralized dentin
Please be aware that the book you have requested cannot be checked out. If you would like to checkout this book, you can reserve another copy
We have requested the book for you!
Your request is successful and it will be processed during the Library working hours. Please check the status of your request in My Requests.
Oops! Something went wrong.
Looks like we were not able to place your request. Kindly try again later.
Journal Article
Effects of bioactive glass incorporation into glass ionomer cement on demineralized dentin
2021
Overview
The effects of the incorporation of sodium-free bioactive glass into glass ionomer cement (GIC) on the demineralized dentin are studied. Four experimental groups with various amounts of BAG in GIC were considered: BG0 group: 0 wt% (control); BG5 group: 5 wt%; BG10 group: 10 wt%; BG20 group: 20 wt%. The GIC surface and GIC-approximated demineralized dentin surfaces were evaluated using field emission scanning electron microscopy (FE–SEM). X-ray diffraction (XRD) analysis was performed to evaluate the chemical changes in the GIC-approximated dentin surface. In addition, a shear bond strength test was performed to evaluate the effects of BAG incorporation on the bond strength of GIC. FE–SEM analysis indicated that BAG-incorporated GICs formed distinct precipitates on their surface. Precipitates were also formed on the GIC-approximated demineralized dentin surface. It was more obvious when the amount of BAG increased. In the XRD analysis, fluorapatitie (FAP) peaks were detected in the BG5, BG10, and BG20 groups. There was no significant difference in the shear bond strength among all experimental groups. BAG-incorporated GIC precipitated FAP crystals underlying demineralized dentin surface without affecting bond strength. This study suggests the possibility of BAG as a beneficial additive in GIC.