Microstructure and properties study of Mg2-xYxNi0.9Co0.1 (x = 0, 0.1, 0.2, 0.3) hydrogen storage alloys

Huang, Feng, Zhou, Binjun, Li, Defa, Li, Yanzhou, Zhang, Wei

2023

Overview

To enhance the hydrogen storage performance of Mg-Ni system alloys, multi-elemental alloys incorporating Y element, namely Mg2-xYxNi0.9Co0.1 (x = 0, 0.1, 0.2, 0.3), were synthesized through ball milling and sintering. The microstructures of Mg2-xYxNi0.9Co0.1 (x = 0, 0.1, 0.2, 0.3) alloys were characterized using XRD and SEM/EDS techniques, and the hydrogen storage properties of Mg2Ni0.9Co0.1 and Mg1.7Y0.3Ni0.9Co0.1 alloys were evaluated via the Sieverts method. At a sintering temperature of 500 °C, the Y element existed in the form of Y/Y2O3 phases and displayed no reactivity with other alloy constituents. The addition of Y enhanced the activation performance of Mg-Ni system alloys, because it takes 2 times for Mg1.7Y0.3Ni0.9Co0.1 alloy to complete activation, while Mg2Ni0.9Co0.1 needs 3, albeit causing a slight reduction from 3.6 wt% to 3.2 wt% in the hydrogen storage capacity when Y replaced Mg. The enthalpy of hydrogen desorption of Mg1.7Y0.3Ni0.9Co0.1 alloy was 57.4 kJ mol−1 H2, which was significantly lower than that of Mg2Ni0.9Co0.1 (68.0 kJ mol−1 H2) and Mg2Ni alloy (64.4 kJ mol−1 H2), indicating improved thermodynamic properties. Moreover, the apparent activation energy of Mg2Ni0.9Co0.1 (71.48 kJ mol−1 H2) was lower than that of Mg1.7Y0.3Ni0.9Co0.1 (83.62 kJ mol−1 H2), implying that the addition of Y reduced the kinetic properties.

• Publisher: IOP Publishing
• Subject: Alloying elements / Alloys / Ball milling / Enthalpy / Hydrogen / Hydrogen storage materials / hydrogen storage properties / Metallurgical constituents / Mg-based hydrogen storage alloys / Microstructure / properties / Sintering / Storage capacity / Thermodynamic properties / Yttrium oxide